Hyperbranched polymers with high molecular weights were synthesized by t -BuP ₂ -catalyzed oxa-Michael addition polymerization of trifunctional hydroxyl and diacrylate monomers.

Self-condensing vinyl polymerization (SCVP) provides an efficient approach for synthesis of hyperbranched polymers. However, most of the inimers employed for SCVP need to be synthesized before use. Here, we report a facile strategy to synthesize hyperbranched polymers under mild conditions by using a commercially available hydroxyl-substituted methacrylate as the inimer. The hyperbranched structures of the resulting polymers were confirmed by nuclear magnetic resonance, differential scanning calorimetry and size-exclusion chromatography equipped with online light scattering and viscosity detectors. The synthesis can be performed under mild reaction conditions. Particularly, this approach can be applied to not only the SCVP of vinyl monomers but also the self-condensing ring-opening polymerization of cyclic esters for preparation of hyperbranched polyesters. The present study provides a facile strategy to synthesize hyperbranched polymers.

Radical solvent-free suspension polymerization of styrene with 3-mercapto hexyl-methacrylate (MHM) as the branching monomer has been carried out using 2,2′-azobisisobutyronitrile (AIBN) as the initiator to prepare branched polymer beads of high purity. The molecular weight and branching structure of the polymers have been characterized by triple detection size exclusion chromatography (TD-SEC), proton nuclear magnetic resonance spectroscopy (¹H-NMR), and Fourier transform infrared spectroscopy (FTIR). The glass transition temperature and rheological properties have been measured by using differential scanning calorimetry (DSC) and rotational rheometry. At mole ratios of MHM to AIBN less than 1.0, gelation was successfully avoided and branched polystyrene beads were prepared in the absence of any solvent. Branched polystyrene has a relatively higher molecular weight and narrower polydispersity (M_w.MALLS = 1,036,000 g·mol⁻¹, M_w/M_n = 7.76) than those obtained in solution polymerization. Compared with their linear analogues, lower glass transition temperature and decreased chain entanglement were observed in the presently obtained branched polystyrene because of the effects of branching.

Phosphazene base, t-BuP₂, was employed to catalyze the proton transfer polymerization (PTP) of 2-hydroxyethyl acrylate (HEA), and PTP was further combined with ring-opening polymerization (ROP) to exploit a new type of hybrid copolymerization. The studies on homopolymerization showed that t-BuP₂ was a particularly efficient catalyst for the polymerization of HEA at room temperature, giving an excellent monomer conversion. Throughout the polymerization, transesterification reactions were unavoidable, which increased the randomness in the structures of the resulting polymers. The studies on copolymerization showed that t-BuP₂ could simultaneously catalyze the hybrid copolymerization via the combination of PTP and ROP at 25 °C. During copolymerization, HEA not only provided hydroxyl groups to initiate the ROP of ε-caprolactone (CL) but also participated in the polymerization as a monomer for PTP. The copolymer composition was approximately equal to the feed ratio, demonstrating the possibility to adjust the polymeric structure by simply changing the monomer feed ratio. This copolymerization reaction provides a simple method for synthesizing degradable functional copolymers from commercially available materials. Hence, it is important not only in polymer chemistry but also in environmental and biomedical engineering.