Controlling the interlayer coupling by tuning lattice parameters through pressure engineering is an important route for tailoring the optoelectronic properties of two-dimensional materials. In this work, we report a pressure-dependent study on the exciton transitions of bilayer MoS₂ exfoliated on a diamond anvil surface. The applied hydrostatic pressure changes from ambient pressure up to 11.05 GPa using a diamond anvil cell device. Raman, photoluminescence, and reflectivity spectra at room temperature are analyzed to characterize the interlayer coupling of this bilayer system. With the increase of pressure, the indirect exciton emission disappears completely at about 5 GPa. Importantly, we clearly observed the interlayer exciton from the reflectivity spectra, which becomes invisible at a low pressure around 1.26 GPa. This indicates that the interlayer exciton is very sensitive to the hydrostatic pressure due to the oscillator strength transfer from the direct transition to the indirect one.

In 2H stacking bilayer MoS₂, the exciton with an interlayer nature has been evidenced due to the hybridization of hole states among both layers. The transition energy of this interlayer exciton is located between the A and B excitons. In this work, we investigate the evolution of optical properties in stacking MoS₂ bilayers with the twisted angles ranging from 0° to 60°, especially focusing on the interlayer exciton. The clear modulations of the exciton responses are observed by the room-temperature reflectance. The interlayer exciton transition is observed in the artificial stacking bilayer MoS₂ with the twisted angle around 60°. We found that the interlayer exciton is very sensitive to the twisted angle. Once the stacking angle deviates the 2H stacking by a few degrees, the interlayer transition is quenched. This is due to the bilayer symmetry and interlayer coupling of this unique system.