A higher density of large-angle grain boundaries in palladium membranes promotes hydrogen diffusion whereas small-angle grain boundaries suppress it. In this paper, the microstructure formation in 10 µm thick palladium membranes is tuned to achieve a submicronic grain size above 100 nm with a high density of large-angle grain boundaries. Moreover, changes in the grain boundaries’ structure is investigated after exposure to hydrogen at 300 and 500 °C. To attain large-angle grain boundaries in Pd, the coating was performed on yttria-stabilized zirconia/porous Crofer 22 APU substrates (intended for use later in an ultracompact membrane reactor). Two techniques of plasma sprayings were used: suspension plasma spraying using liquid nano-sized powder suspension and vacuum plasma spraying using microsized powder as feedstock. By controlling the process parameters in these two techniques, membranes with a comparable density of large-angle grain boundaries could be developed despite the differences in the fabrication methods and feedstocks. Analyses showed that a randomly oriented submicronic structure could be attained with a very similar grain sizes between 100 and 500 nm which could enhance hydrogen permeation. Exposure to hydrogen for 72 h at high temperatures revealed that the samples maintained their large-angle grain boundaries despite the increase in average grain size to around 536 and 720 nm for vacuum plasma spraying and suspension plasma spraying, respectively.

Additive manufacturing of metals has attracted significant attention across various industries. However, its adoption in certain chemical and energy sectors remains constrained by the absence of optimized alloys tailored for high temperatures and corrosive environments. This study explores the laser-based powder bed fusion processing of Crofer 22 APU, a high-temperature, corrosion-resistant alloy ideal for applications such as methane steam reforming reactors, high-temperature fuel cells, and palladium membrane supports. Systematic optimization of laser parameters including laser power, hatch distance, point distance, and building angles was conducted for both dense and porous objects. Dense parts achieved a relative density of 0.9999 and surface roughness of Sa= 41.27±1.48 on a 45 $$^\circ$$ ∘ overhang. Porous samples showed a porosity range of 28.6 to 55.5% and surface roughness Sa 22.2 $$\upmu$$ μ m to 45.9 $$\upmu$$ μ m as hatch distance increased from 0.12 mm to 0.16 mm. Additionally, an 8YSZ coating applied via screen printing demonstrated the impact of hatch distance and laser power on surface quality. The combination of additive manufacturing of Crofer 22 APU and screen printing of 8YSZ simplifies the preparation of metallic supports for Pd-based membranes, reducing fabrication time and cost by shortening the number of preparation steps. This technique offers a promising approach for scaling up membranes and membrane reactors.

The publication of this article unfortunately contained mistakes. One sentence in abstract was not correct. The corrected sentence is given below. Wrong senctence: Porous samples showed a porosity range of 28.655.5% and surface roughness Sa 22.2 μ m to 45.9 μ m as hatch distance increased from 0.12 mm to 0.16 mm. Correct sentence: Porous samples showed a porosity range of 28.6 to 55.5% and surface roughness Sa 22.2 μ m to 45.9 μ m as hatch distance increased from 0.12 mm to 0.16 mm.