The development of phase change materials (PCM) for thermal energy storage is a promising technology. However, the liquid PCM leaks and low thermal conductivity limit the practical PCM applications. This article aims to solve these problems; it presents the preparation and thermal characterisation of PCM enhanced by carbon-based nanoparticles. The polyethene glycol 6000 (PEG 6000) is used as PCM and multi-walled carbon nanotubes (MWCNTs) as a shell matrix and thermal conductivity enhancer. The sample was prepared by the sonification method under vacuum conditions. Fourier transform infra-red spectroscopy (FT-IR) and thermo-gravimetric analysis (TGA) tested the chemical and thermal compatibility of the prepared samples. The storage performances are tested by modulated differential scanning calorimetry characterisation. The nano-enhanced-PCM (NPCM) with 1 wt% MWCNTs showed excellent shape stability without any liquid leakage when the temperature was about 110 °C for 30 minutes. Drying method has a significant effect on the thermal storage capacity of the NPCM. The melting, solidification points and the latent heats of the NPCM were measured as 61.75, 35.50 °C, and 174.24, 167.84 J g⁻¹, respectively. Meanwhile, the specific heat is 2.63 J g⁻¹°C⁻¹ for the solid-state and 2.14 J g⁻¹°C⁻¹ for the liquid-state. The thermal conductivity of pristine PEG was improved by 49%.

In the phosphate industry, the thickening process is vital to increasing the solid slurry concentration and to recovering water that is as clear as possible. The performance of the thickening process depends mainly on the coagulation–flocculation effect. The thickening process is based on flocculant agents to concentrate particles: flotation and washing plant rejects as large flocs, which accelerate their sedimentation velocity. The phosphate industry worldwide uses synthetical flocculants such as polyacrylamides. These flocculants are non-biodegradable, limiting the process efficiency regarding cost and harmful effects on the environment. This study proposes cactus cladodes juice as an eco-friendly alternative to industrial flocculants. The particle size of the phosphate samples ranges from 0 μm to 160 μm, with a solid concentration of 8%. This bioflocculant allowed for an increase in sedimentation velocity of 95% compared with the case without flocculant. The optimal amount of cactus bioflocculant for decanting 1 tonne of phosphate pulp at pH 7–8 is 1.12 kg. Special attention is paid to understanding the flocculation mechanism. The results of the physicochemical characterization show that the flocculant biopolymers have similar characteristics to anionic polyacrylamide. This work indicates the promising application of the cactus juice bioflocculant in phosphate washing plants.