Low-carbon Ti-Mo microalloyed steels represent a new generation of high strength steels for automobile sheet. Excellent indicators of difficult-to-combine technological, strength, and other service properties are achieved due to the superposition of a dispersed ferrite matrix and a bulk system of nanoscale carbide precipitates. Recently, developments are underway to optimize thermo-deformation processing for the most efficient use of phase precipitates. The review summarizes and analyzes the results of studies of mechanical properties depending on the chemical composition and parameters of hot deformation of low-carbon Ti-Mo microalloyed steels. Particular attention is paid to the features of the formation and the influence of various types of phase precipitates and the dispersion of the microstructure on mechanical properties. The advantages of Ti-Mo microalloying system and the tasks requiring further solution are shown.

The features of current state of metallurgical technology and materials science of mass high-grade steels are viewed. A promising direction for principle improvement of the complex of properties and qualitative characteristics of steel including those, which are difficult to combine, is shown. It is the development of adequate physico-chemical methods of prediction and efficient technology methods of management of non-metallic inclusions, forms of presence of impurities, phases precipitations, structural state, including uniformity over the volume of metal. Additionally this approach allows reducing costs and expanding the raw material base. Its effectiveness is illustrated by the results of research carried out for a number of groups of mass high-quality steels.

High-strength microalloyed steels are widely used in various branches of technology and industry due to the simultaneous combination of high indicators of strength, ductility, fatigue, corrosion resistance, and other service properties. This is achieved due to the reasonable choice of the optimal chemical composition and parameters of temperature-deformation treatment of steel that provide a synergistic effect on the dispersed microstructure and characteristics of excess phase precipitates, which control the achievement of these difficult-to-combine properties of rolled products. Additionally, the improvement of the level and stability of these properties, as well as the prevention of the occurrence of defects, is largely determined by the indicators of the homogeneity of the composition, structure by volume and manufacturability of the metal, and primarily hot ductility, which are controlled by the presence of precipitation of excess phases, including microalloying elements. In accordance with the circumstances noted, in the present review, a generalization, systematization, and analysis of the results of the studies are conducted on the effect of phase precipitates on the hot ductility and homogeneity of composition and structure, depending on the chemical composition and parameters of the temperature-deformation treatment of steel.

The most promising direction for obtaining a unique combination of difficult-to-combine properties of low-carbon steels is the formation of a dispersed ferrite microstructure and a volumetric system of nanoscale phase precipitates. This study was aimed at establishing the special features of the composition influence on the characteristics of the microstructure, phase precipitates, and mechanical properties of hot-rolled steels of the ferritic class. It was carried out by transmission electron microscopy and testing the mechanical properties of metal using 8 laboratory melts of low-carbon steels microalloyed by V, Nb, Ti, and Mo in various combinations. It was found that block ferrite prevails in the structure of steel cooled after hot rolling at a rate of 10–15 °C/s. Lowering of the microalloying components content leads to a decrease in the block ferrite fraction to 20–35% and the dominance of polygonal ferrite. The presence of nanoscale carbide (carbonitride) precipitates of austenitic and interphase/mixed types was detected in the rolled steels. It was established that the tendencies of changes in the characteristics of the structural state and present phase precipitates correlate well with obtained values of strength properties. The advantages of titanium-based microalloying systems in comparison with vanadium-based are shown.