Endowing a single material with various types of luminescence, that is, exhibiting a simultaneous optical response to different stimuli, is vital in various fields. A photoluminescence (PL)‐ and mechanoluminescence (ML)‐based multifunctional sensing platform is built by combining heterojunctioned ZnS/CaZnOS:Mn²⁺ mechano‐photonic materials using a 3D‐printing technique and fiber spinning. ML‐active particles are embedded in micrometer‐sized cellulose fibers for flexible optical devices capable of emitting light driven by mechanical force. Individually modified 3D‐printed hard units that exhibit intense ML in response to mechanical deformation, such as impact and friction, are also fabricated. Importantly, they also allow low‐pressure sensing up to ≈100 bar, a range previously inaccessible by any other optical sensing technique. Moreover, the developed optical manometer based on the PL of the materials demonstrates a superior high‐pressure sensitivity of ≈6.20 nm GPa⁻¹. Using this sensing platform, four modes of temperature detection can be achieved: excitation‐band spectral shifts, emission‐band spectral shifts, bandwidth broadening, and lifetime shortening. This work supports the possibility of mass production of ML‐active mechanical and optoelectronic parts integrated with scientific and industrial tools and apparatus.

This work sheds light on the pump power impact on the performance of luminescent thermometers, which is often underestimated by researchers. An up-converting, inorganic nanoluminophore, YVO₄:Yb³⁺,Er³⁺ (nanothermometer) was synthesized using the hydrothermal method and a subsequent calcination. This nanomaterial appears as a white powder composed of small nanoparticles (≈20 nm), exhibiting a very intense, green upconverted luminescence (λ_ex = 975 nm), visible to the naked eye. Its emission spectrum consists of four Er³⁺ bands (500–850 nm) and one Yb³⁺ band (>900 nm). The obtained compound exhibits temperature-dependent luminescence properties, hence it is used as an optical nanosensor of temperature. The determined band intensity ratios of the non-thermally coupled levels (non-TCLs) of Yb³⁺/Er³⁺ and thermally coupled levels (TCLs) of Er³⁺ are correlated with temperature, and they are used for ratiometric sensing of temperature. The effects of the pump (NIR laser) power on the luminescence properties of the material, including band intensity ratios, absolute and relative sensitivities and temperature resolution are analysed. It was pointed out that the applied laser power has a huge impact on the values of the aforementioned thermometric parameters, and manipulating the laser power can significantly improve the performance of optical nanothermometers.

The use of functional nanomaterials and their combination with organic polymers leads to the formation of advanced composites and hybrid inorganic–organic systems having unique properties. The use of such materials as anti-counterfeiting agents (invisible under ambient conditions) is crucial for modern security systems and for further identification of labelled items and documents in various industrial applications. Here, the fabrication of functional paper by in situ incorporation of luminescent cellulose fibres into its structure, during the formation of paper pulp, is shown. In order to produce luminescent fibres, an in situ modification is made during the spinning process, using lanthanide-doped upconverting nanoparticles (SrF₂:Yb³⁺,Er³⁺). At first glance (in daylight), the functionalized paper cannot be distinguished from its unmodified form. However, when exposed to invisible near-infrared laser light (975 nm), bright green illumination appears. The modified paper preserves good mechanical durability, which is important for its potential for further processing in documents and other commercially available forms. Protecting documents and various materials with this kind of paper may open new horizons in materials engineering, forensics, and other industrial applications.

In this study, an optical thermometer based on regenerated cellulose fibers modified with YF₃: 20% Yb³⁺, 2% Er³⁺ nanoparticles was developed. The presented sensor was fabricated by introducing YF₃ nanoparticles into cellulose fibers during their formation by the so-called Lyocell process using N-methylmorpholine N-oxide as a direct solvent of cellulose. Under near-infrared excitation, the applied nanoparticles exhibited thermosensitive upconversion emission, which originated from the thermally coupled levels of Er³⁺ ions. The combination of cellulose fibers with upconversion nanoparticles resulted in a flexible thermometer that is resistant to environmental and electromagnetic interferences and allows precise and repeatable temperature measurements in the range of 298–362 K. The obtained fibers were used to produce a fabric that was successfully applied to determine human skin temperature, demonstrating its application potential in the field of wearable health monitoring devices and providing a promising alternative to thermometers based on conductive materials that are sensitive to electromagnetic fields.