The objective of this work is to study the peculiarities of structural organization, morphology, thermomechanical, electrical and antimicrobial properties of nanocomposites based on pectin-polyethyleneimine interpolyelectrolyte complexes and silver nanoparticles in dependence on the type of reducing agent being applied for chemical reduction of silver ions in the interpolyelectrolyte-metal complexes. The average size of Ag nanoparticles is shown to be increased with decreasing of the activity of reducing agent (E₀) and equals to 3.8 nm, 4.3 nm, and 15.8 nm, respectively, when engaging sodium borohydride (–1.24 V), hydrazine (–1.15 V) and ascorbic acid (–0.35 V). Moreover, it was found that the crystallite size of Ag nanoparticles also had the smallest value for nanocomposites obtained involving NaBH₄ as reducing agent. Ag-containing nanocomposites prepared by reduction of silver ions in interpolyelectrolyte-metal complexes while applying a range of reducing agents are characterized by different electrical properties and polymer matrix’ glass transition temperature. The influence of silver nanoparticles’ size incorporated in the polymer matrix on the antimicrobial activity of nanocomposites has been established. The inhibition zone diameter of Staphylococcus aureus and Escherichia coli was higher for nanocomposites obtained using sodium borohydride and hydrazine compared to nanocomposites where ascorbic acid was used as the reducing agent.

Green synthesis of silver-containing nanocomposites based on polylactide (PLA) was carried out in two ways. With the use of green tea extract, Ag⁺ ions were reduced to silver nanoparticles with their subsequent introduction into the PLA (mechanical method) and Ag⁺ ions were reduced in the polymer matrix of PLA-AgPalmitate (PLA-AgPalm) (in situ method). Structure, morphology and thermophysical properties of nanocomposites PLA-Ag were studied by FTIR spectroscopy, wide-angle X-ray scattering (WAXS), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC) methods. The antimicrobial, antiviral, and cytotoxic properties were studied as well. It was found that the mechanical method provides the average size of silver nanoparticles in the PLA of about 16 nm, while in the formation of samples by the in situ method their average size was 3.7 nm. The strong influence of smaller silver nanoparticles (3.7 nm) on the properties of nanocomposites was revealed, as with increasing nanosilver concentration the heat resistance and glass transition temperature of the samples decreases, while the influence of larger particles (16 nm) on these parameters was not detected. It was shown that silver-containing nanocomposites formed in situ demonstrate antimicrobial activity against gram-positive bacterium S. aureus, gram-negative bacteria E. coli, P. aeruginosa, and the fungal pathogen of C. albicans, and the activity of the samples increases with increasing nanoparticle concentration. Silver-containing nanocomposites formed by the mechanical method have not shown antimicrobial activity. The relative antiviral activity of nanocomposites obtained by two methods against influenza A virus, and adenovirus serotype 2 was also revealed. The obtained nanocomposites were not-cytotoxic, and they did not inhibit the viability of MDCK or Hep-2 cell cultures.