Additive manufacturing (AM), or 3D printing, is drawing considerable contemporary interest due to its characteristics of high material utilization, great flexibility in product design, and inherent moldless process. Arc-based AM (AAM) is a promising AM method with high deposition rate and favorable buildup quality. Components made by AAM are fabricated through superimposed weld beads deposited from metal wire. Unlike laser-based additive manufacturing, AAM is more difficult to control. Because of the large energy input of the energy source and the liquidity of the melting metal material, bottleneck problems like shrinkage porosity, cracking, residual stresses, and deformation occur. Resultant poor geometrical accuracy and mechanical property keep AAM from industrial application. Especially in the aerospace industry, structural and mechanical property specifications are stringent and critical. This paper presents a novel hybrid manufacturing method by using hot-rolling process to assist the arc welding to solve the above problems. Initially, a miniature metamorphic rolling mechanism (MRM) was developed using metamorphic mechanism theory. Configuration and topology of the MRM can change according to the feature of the components to roll the top and lateral surfaces of the bead. Subsequently, three single-pass multilayer walls were built, respectively, for comparison. The rolled results show significant improvement in geometrical accuracy of the built features. Tensile test results demonstrate improvement in mechanical properties. The improved mechanical properties of rolled specimens are superior to wrought material in travel direction. Microstructure comparisons indicate columnar grains observed in vertical direction and fusion zones were suppressed. Eventually, fabrication of a large-scale aerospace component validates the feasibility of industry application for the hybrid manufacturing technology.

As an effective method for the fabrication of miniature metallic parts, the development of micro-forming process (MFP) is still restricted by the existence of size effect. To improve the micro-forming performance of metal material, ultrasonic vibration assisted MFP had been studied extensively for its superiorities in improving materials flow stress and reducing interfacial friction. However, from the literature available, the high frequency vibration was usually found to be superimposed on the forming tool while seldom on the workpiece. Our group developed a special porous sonotrode platform which can realize tool vibration and workpiece ultrasonic vibration independently. In this work, ultrasonic micro-extrusion experiments for copper T2 material under tool vibration and the workpiece vibration condition, respectively, were conducted for comparing the micro-forming characteristic of different vibration modes. The micro-extrusion experiment results of copper T2 show that the lower extrusion flow stress, the higher micro-extrusion formability and surface micro-hardness, and more obvious grain refinement phenomenon can be obtained under the workpiece vibration condition compared with that of tool vibration. These findings may enhance our understanding on different ultrasonic forming mechanisms and energy transmission efficiency under two different vibration modes.