The effect of crystallography on transgranular chloride-induced stress corrosion cracking (TGCISCC) of arc welded 304L austenitic stainless steel is studied on >300 grains along crack paths. Schmid and Taylor factor mismatches across grain boundaries (GBs) reveal that cracks propagate either from a hard to soft grain, which can be explained merely by mechanical arguments, or soft to hard grain. In the latter case, finite element analysis reveals that TGCISCC will arrest at GBs without sufficient mechanical stress, favorable crystallographic orientations, or crack tip corrosion. GB type does not play a significant role in determining TGCISCC cracking behavior nor susceptibility. TGCISCC crack behaviors at GBs are discussed in the context of the competition between mechanical, crystallographic, and corrosion factors.

Depth-sensing transmission electron microscopic (TEM) in situ mechanical testing has become widely utilized for understanding deformation in irradiated materials. Until now, compression pillars have primarily been used to study the elastic properties and yield of irradiated materials. In this study, we utilize TEM in situ compression pillars to investigate plastic deformation in two ion-irradiated alloys: Fe–9% Cr oxide dispersion strengthened (ODS) alloy and nanocrystalline Cu–24% Ta. We develop an algorithm to automate the extraction of instantaneous pillar dimensions from TEM videos, which we use to calculate true stress–strain curves and strain hardening exponents. True stress–strain curves reveal intermitted plastic flow in all specimen conditions. In the Fe–9% Cr ODS, intermitted plastic flow is linked to strain bursts observed in TEM videos. Low strain hardening or strain softening is observed in all specimen conditions. TEM videos link the strain softening in irradiated Fe–9% Cr ODS to dislocation cross-slip, and in Cu–24% Ta to grain boundary sliding.