Innovative textile-based washable polymer solar cells are realized by suppressing the hydrolysis of the encapsulation barrier with a SiO ₂ –polymer composite.

Free-form optoelectronic devices can provide hyper-connectivity over space and time. However, most conformable optoelectronic devices can only be fabricated on flat polymeric materials using low-temperature processes, limiting their application and forms. This paper presents free-form optoelectronic devices that are not dependent on the shape or material. For medical applications, the transferable OLED (10 μm) is formed in a sandwich structure with an ultra-thin transferable barrier (4.8 μm). The results showed that the fabricated sandwich-structure transferable OLED (STOLED) exhibit the same high-efficiency performance on cylindrical-shaped materials and on materials such as textile and paper. Because the neutral axis is freely adjustable using the sandwich structure, the textile-based OLED achieved both folding reliability and washing reliability, as well as a long operating life (>150 h). When keratinocytes were irradiated with red STOLED light, cell proliferation and cell migration increased by 26 and 32%, respectively. In the skin equivalent model, the epidermis thickness was increased by 39%; additionally, in organ culture, not only was the skin area increased by 14%, but also, re-epithelialization was highly induced. Based on the results, the STOLED is expected to be applicable in various wearable and disposable photomedical devices.

Stretchable displays attract significant attention because of their potential applications in wearable electronics, smart textiles, and human-conformable devices. This paper introduces an electrically stable, mechanically ultra-robust, and water-resistant stretchable OLED display (SOLED) mounted on a stress-relief pillar platform. The SOLED is fabricated on a thin, transparent polyethylene terephthalate (PET) film using conventional vacuum evaporation, organic-inorganic hybrid thin film encapsulation (TFE), and a nonselective laser patterning process. This simple and efficient process yields an OLED display with exceptional stretchability, reaching up to 95% strain and outstanding durability, enduring 100,000 stretch-release cycles at 50% strain. Operational lifetime and water-resistant storage lifetime measurements confirm that the TFE provides effective protection even after the nonselective laser patterning process. A 3 × 3 array SOLED display module mounted on a stress-relief pillar platform is successfully implemented, marking the first case of water-resistant display array operation in the field of SOLEDs. This work aims to develop practical stretchable displays by offering a reliable fabrication method and device design for creating mechanically robust and adaptable displays, potentially paving the way for future advances in human-conformable electronics and other innovative applications.