A series of CuO-based catalysts supported on the α-MnO₂ nanowire were facilely synthesized and employed as the CO oxidation catalysts. The achieved catalysts were systematically characterized by XRD, SEM, EDS-mapping, XPS and H₂-TPR. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of different loading methods, calcination temperatures and CuO loading on the low temperature catalytic activity of the catalyst were investigated and compared with the traditional commercial MnO₂ catalyst with a block structure. It was found that the slenderness ratio of a CuO/α-MnO₂ nanowire catalyst decreases with the increase in CuO loading capacity. The results showed that when CuO loading was 3 wt%, calcination temperature was 200 °C and the catalyst that was supported by the deposition precipitation method had the highest catalytic activity. Besides, the α-MnO₂ nanowire-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial MnO₂-supported catalyst. In conclusion, the CuO-based catalysts that are supported by α-MnO₂ nanowires are considered as a series of promising CO oxidation catalysts.

As a toxic pollutant, carbon monoxide (CO) usually causes harmful effects on human health. Therefore, the thermally catalytic oxidation of CO has received extensive attention in recent years. The CuO-based catalysts have been widely investigated due to their availability. In this study, a series of transition metal oxides (Fe₂O₃, Co₃O₄ and NiO) promoted CuO-based catalysts supported on the α-MnO₂ nanowire catalysts were prepared by the deposition precipitation method for catalytic CO oxidation reactions. The effects of the loaded transition metal type, the loading amount, and the calcination temperature on the catalytic performances were systematically investigated. Further catalyst characterization showed that the CuO/α-MnO₂ catalyst modified with 3 wt% Co₃O₄ and calcined at 400 °C performed the highest CO catalytic activity (T₉₀ = 75 °C) among the investigated catalysts. It was supposed that the loading of the Co₃O₄ dopant not only increased the content of oxygen vacancies in the catalyst but also increased the specific surface area and pore volume of the CuO/α-MnO₂ nanowire catalyst, which would further enhance the catalytic activity. The CuO/α-MnO₂ catalyst modified with 3 wt% NiO and calcined at 400 °C exhibited the highest surface adsorbed oxygen content and the best normalized reaction rate, but the specific surface area limited its activity. Therefore, the appropriate loading of the Co₃O₄ modifier could greatly enhance the activity of CuO/α-MnO₂. This research could provide a reference method for constructing efficient low-temperature CO oxidation catalysts.