The aim of this systematic review was to determine the optimal printing parameters for the producing of fused deposition modeling (FDM) 3D-printed polyetheretherketone (PEEK) elements with mechanical properties suitable for dental restorations. Indeed, the mechanical properties are a critical prerequisite for the study of other parameters, such as physical, aesthetic and biological properties. An exhaustive electronic search was carried out in the PubMed, Embase and Web of knowledge databases to gather all the studies evaluating the influence of the printing parameters on the obtained mechanical properties of FDM 3D-printed PEEK elements were selected. Initially, the search resulted in 614 eligible papers. Independent screenings of the abstracts were performed by two authors to identify the articles related to the question. Twenty-nine studies were selected, of which eleven were further excluded after reading of the full text, and finally, eighteen articles were included in this review. The studies were difficult to compare due to the variability of the printing parameters and the types of PEEK. However, it seems interesting to use a high infill rate, a high chamber temperature close to that of the printing temperature and a heat post-treatment to obtain 3D PEEK elements presenting properties adapted to use as dental restorations. The analysis of the available literature suggested that the properties of PEEK could make it an interesting material in dental restorations to be performed with FDM additive manufacturing.

This study aims to compare the shear bond strength (SBS) of a direct resin composite to CAD-CAM resin composite blocks treated with different surface treatments: micromechanical, chemical or a combination of both. Eight CAD-CAM resin composite blocks, namely Brilliant Crios, Cerasmart 270, Vita Enamic, Grandio block, Katana Avencia, Lava Ultimate, Tetric CAD and Shofu Block HC were chosen. The micromechanical surface treatment protocols tested were hydrofluoric acid, polyacrylic acid or sandblasting, and the chemical one was a universal primer. These treated CAD-CAM blocks were tested to determine the SBS of a light-curing composite resin Z100 bonded to their surface. Two-way ANOVA followed by Tukey’s post hoc test was used to investigate the difference in SBS. Failures were analyzed by Fisher’s exact test. Bonding interfaces were examined by scanning electron microscopy. The micromechanical surface treatments give the highest SBS values: sandblasting appears to be the most efficient procedure for dispersed filler composite blocks, while hydrofluoric acid etching is preferable for polymer-infiltrated ceramic network (PICN) blocks. The use of universal primer does not improve SBS values on dispersed filler composite blocks. For PICN blocks, the use of universal primer significantly increases SBS values when combined with hydrofluoric acid etching.

Objective: Evaluation of the Shear bond strength over zirconia and titanium alloy and degree of conversion of extraoral compared to intraoral self-adhesive resin cements. Materials and methods: Nine bonding protocols were carried out on zirconia 4Y-TZP and titanium alloy (Ti-6Al-4V). Seven resin cement (one extraoral and six intraoral) were tested in the shear bond strength test and the degree of conversion measurements. Results: The significantly highest value was obtained for Monobond Plus + Multilink Hybrid Abutment, the extraoral resin cement for both titanium alloy (35.1 MPa) and zirconia (32.9 MPa). For each resin, significantly higher DC values were obtained for the dual-cure mode compared with the self-cure mode. Regardless of the cure mode, Nexus Universal reached the highest DC (78.4%). Discussion/Conclusions: In this study, the extraoral self-curing resin cement showed the higher bond strength values on zirconia and titanium alloy when associated with a universal primer. Some intraoral dual-cure resin cements showed closed performances when used with universal primers. There is no direct correlation between the degree of conversion of the resin cement and the shear bond strength obtained on the prosthetic materials tested.

The main cause of failure in bonded ceramic restorations is material fracture due to excessive stress concentration at the base of the prosthesis. The design of restorative functionally graded materials (FGM) could represent a major advance in dissipating mechanical stresses during occlusal contacts. The aim of this paper is to carry out a complete factorial design of finite element analyses to optimize a multilayer FGM introduced at the bottom of an overlay prosthesis. The number and thickness of layers vary within a spectrum compatible with ceramic shaping processes whereas Young's moduli variations are set in the range of dental tissues. For a 1.5-mm thick prosthesis, the optimal FGM configuration appears to be a 5 layers of 0.2 mm thickness with a linear distribution of Young's modulus from 30 to 70 GPa. This configuration was implemented in a 3D model of a restored tooth with realistic geometry to validate the proof-of-concept.

Dental erosions and molar-incisor hypomineralization are two common dental pathologies requiring minimally invasive restorations such as overlays. The currently used restorative materials are diver...

Objective:Evaluation of the Shear bond strength over zirconia and titanium alloy and degree of conversion of extraoral compared to intraoral self-adhesive resin cements. Materials and methods: Nine bonding protocols were carried out on zirconia 4Y-TZP and titanium alloy grade V. Seven resin cement were tested in the shear bond strength test and the degree of conversion measurements. One extraoral (Multilink hybrid abutment) and six intraoral (G-cem One, SpeedCem Plus, RelyX Universal, Panavia SA Universal, Nexus Universal, Totalcem). Results: The significantly highest value was obtained for Monobond Plus + Multilink Hybrid Abutment, the extraoral resin cement for both titanium alloy and zirconia. For each resin, significantly higher DC values were obtained for the dual-cure mode compared with the self-cure mode. Regardless of the cure mode, Nexus Universal reached the highest DC. Discussion/Conclusions: In this study, the extraoral self-curing resin cement showed the best bond strength values on zirconia and titanium alloy when associated with a universal primer. Some intraoral dual-cure resin cements showed closed performances when used with universal primers. There is no direct correlation between the degree of conversion of the resin cement and the shear bond strength obtained on the prosthetic materials tested.