MAX phases, characterized as nanolaminates of ternary carbides/nitrides structure, possess a unique combination of ceramic and metallic properties, rendering them pivotal in materials research. In this study, chromium aluminum carbide ternary compounds, Cr₂AlC (211), Cr₃AlC₂ (312), and Cr₄AlC₃ (413) were successfully synthesized with high purity using a facile and cost-effective sol-gel method. Structural, morphological, and chemical characterization of the synthesized phases was conducted to understand the effects of composition changes and explore potential applications. Comprehensive characterization techniques including XRD for crystalline structure elucidations, SEM for morphological analysis, EDX for chemical composition, Raman spectroscopy for elucidation of vibrational modes, XPS to analyze elemental composition and surface chemistry, and FTIR spectroscopy to ensure the functional groups analysis, were performed. X-ray diffraction analysis indicated the high purity of the synthesized Cr₂AlC phase as well as other ternary compounds Cr₃AlC₂ and Cr₄AlC₃, suggesting its suitability as a precursor for MXenes production. Additionally, the antimicrobial activity against Candida albicans and biocompatibility assessments against Escherichia coli (E. coli), Staphylococcus aureus (S. aureus), and HepG2 cell line were investigated. The results demonstrated significant antifungal activity of the synthesized phases against Candida albicans and negligible impact on the viability of E. coli and S. aureus. Interestingly, lower concentrations of Cr₂AlC MAX phase induced cytotoxicity in HepG2 cells by triggering intercellular oxidative stress, while Cr₃AlC₂ and Cr₄AlC₃ exhibited lower cytotoxicity compared to Cr₂AlC, highlighting their potential in biomedical applications.

Recently, quantum-dot-based core/shell structures have gained significance due to their optical, optoelectronic, and magnetic attributes. Controlling the fluorescence lifetime of QDs shells is imperative for various applications, including light-emitting diodes and single-photon sources. In this work, novel Cu-doped CdS/ZnS shell structures were developed to enhance the photoluminescence properties. The objective was to materialize the Cu-doped CdS/ZnS shells by the adaptation of a two-stage high-temperature doping technique. The developed nanostructures were examined with relevant characterization techniques such as transmission electron microscopy (TEM) and ultraviolet–visible (UV–vis) emission/absorption spectroscopy. Studying fluorescence, we witnessed a sharp emission peak at a wavelength of 440 nm and another emission peak at a wavelength of 620 nm, related to the fabricated Cu-doped CdS/ZnS core/shell QDs. Our experimental results revealed that Cu-doped ZnS shells adopted the crystal structure of CdS due to its larger bandgap. Consequently, this minimized lattice mismatch and offered better passivation to any surface defects, resulting in increased photoluminescence. Our developed core/shells are highly appropriate for the development of efficient light-emitting diodes.