The effects of zinc oxide nanoparticles (ZnONPs) on the properties of rice starch–gelatin (RS–G) films were investigated. ZnONPs were synthesized by a green method utilizing Asiatic pennywort (Centella asiatica L.) extract. The ZnONPs were rod-shaped, with sizes ranging from 100–300 nm. An increase in the concentration of ZnONPs significantly (p < 0.05) increased the thickness (0.050–0.070 mm), tensile strength (3.49–4.63 MPa), water vapor permeability (5.52–7.45 × 10⁻¹¹ g m/m² s Pa), and thermal stability of the RS–G–ZnONPs nanocomposite films. On the other hand, elongation at break (92.20–37.68%) and film solubility (67.84–30.36%) were significantly lower (p < 0.05) than that of the control RS–G film (0% ZnONPs). Moreover, the addition of ZnONPs strongly affected the film appearance, color, transmission, and transparency. The ZnONPs had a profound effect on the UV-light barrier improvement of the RS–G film. The crystalline structure of the ZnONPs was observed in the fabricated nanocomposite films using X-ray diffraction analysis. Furthermore, the RS–G–ZnONPs nanocomposite films exhibited strong antimicrobial activity against all tested bacterial strains (Staphylococcus aureus TISTR 746, Bacillus cereus TISTR 687, Escherichia coli TISTR 527, Salmonella Typhimurium TISTR 1470) and antifungal activity toward Aspergillus niger. According to these findings, RS–G–ZnONPs nanocomposite film possesses a potential application as an active packaging: antimicrobial or UV protective.

The effects of green tea extract (GTE) at varying concentrations (0.000, 0.125, 0.250, 0.500, and 1.000%, w/v) on the properties of rice-starch-pectin (RS-P) blend films were investigated. The results showed that GTE addition enhanced (p < 0.05) the antioxidation properties (i.e., total phenolic content, DPPH radical scavenging activity, and ferric reducing antioxidant power) and thickness of the RS-P composite film. The darker appearance of the RS-T-GTE blend films was obtained in correspondence to the lower L* values. However, the a* and b* values were higher toward red and yellow as GTE increased. Though GTE did not significantly alter the film solubility, the moisture content and the water vapor permeability (WVP) of the resulting films were reduced. In addition, the GTE enrichment diminished the light transmission in the UV-Visible region (200–800 nm) and the transparency of the developed films. The inclusion of GTE also significantly (p < 0.05) lowered the tensile strength (TS) and elongation at break (EAB) of the developed film. The FT-IR spectra revealed the interactions between RS-P films and GTE with no changes in functional groups. The antimicrobial activity against Staphylococcus aureus (TISTR 764) was observed in the RS-P biocomposite film with 1% (w/v) GTE. These results suggested that the RS-P-GTE composite film has considerable potential for application as active food packaging.

Bio-based film is an eco-friendly alternative to petroleum-based packaging film. The effects of biocomposite wrapping film enhanced with dragon fruit peel extract (0, 2% w/v, respectively) and currently used commercial packaging film (polypropylene; PP) on coconut milk caramels during storage (30 °C, 75% RH, nine days) were studied. Both 0% and 2% DPE-enriched biocomposite films were thicker and had higher water vapor permeability and solubility than the PP film but poorer mechanical characteristics. In addition, the 2% film possessed antioxidants and antioxidant ability. A FESEM micrograph revealed the rough surface and porous path of the biocomposite films. Over the storage time, the moisture content, water activity, and springiness of the coconut milk caramel candy wrapped in the PP and all DPE-enriched biocomposite films were not significantly altered. However, the lipid oxidation as the thiobarbituric acid reactive substance (TBARS) and hardness of all coconut caramels were significantly (p < 0.05) increased during storage. Furthermore, the hardness of coconut candy covered in the control (0% DPE) biocomposite film was more pronounced on day nine of storage. However, the changes in quality characteristics of the coconut candy wrapped in each film type need to be better established. The investigating factors influencing the quality deterioration of coconut milk candy should be further identified to mitigate their effects and extend the shelf-life of the coconut candy.