Purpose: – This paper aims to carry out tribological experiments to explore the applications of femtosecond laser surface texturing technology on rock bit sliding bearing to enhance the lifetime and working performance of rock bit sliding bearing under high temperature and heavy load conditions. Design/methodology/approach: – Surface textures on beryllium bronze specimen were fabricated by femtosecond laser ablation (800 nm wavelength, 40 fs pulse duration, 1 kHz pulse repetition frequency), and then the tribological behaviors of pin-on-disc configuration of rock bit bearing were performed with 20CrNiMo/beryllium bronze tribo-pairs under non-Newtonian lubrication of rock bit grease. Findings: – The results showed that the surface texture on beryllium bronze specimens with specific geometrical features can be achieved by optimizing femtosecond laser processing via adjusting laser peak power and exposure time; more than 52 per cent of friction reduction was obtained from surface texture with a depth-to-diameter ratio of 0.165 and area ratio of 5 per cent at a shear rate of 1301 s−1 under the heavy load of 20 MPa and high temperature of 120°C, and the lubrication regime of rock bit bearing unit tribo-pairs was improved from boundary to mixed lubrication, which indicated that femtosecond laser ablation technique showed great potential in promoting service life and working performance of rock bit bearing. Originality/value: – Femtosecond laser-irradiated surface texture has the potential possibility for application in rock bit sliding bearing to improve the lubrication performance. Because proper micro dimples showed good lubrication and wear resistance performance for unit tribo-pairs of rock bit sliding bearing under high temperature, heavy load and non-Newtonian lubrication conditions, which is very important to improve the efficiency of breaking rock and accelerate the development of deep-water oil and gas resources.

The influence of spring stiffness and valve quality on the motion behaviors of reciprocating plunger pump discharge valves was investigated by fluid structure interaction (FSI) simulation and experimental analysis. The mathematical model of the discharge valve motion of a 2000-fracturing pump was developed and the discrete differential equations were solved according to FSI and results obtained by ANDINA software. Results indicate that spring stiffness influences the maximum lift, the opening resistance and shut-off lag angle, as well as the fluid velocity of the clearance, the impact stress and the volume efficiency of the pump valve in relation to the valve quality. An optimal spring stiffness parameter of 14.6 N/mm was obtained, and the volumetric efficiency of the pumping valve increased by 4‰ in comparison to results obtained with the original spring stiffness of 10.09N/mm. The experimental results indicated that the mathematical model and FSI method could provide an effective approach for the subsequent improvement of valve reliability, volumetric efficiency and lifespan.

The erosion of the valve core causes valve failure problems. Thus, a novel method to extend the erosion resistance of the valve was innovatively proposed, namely, nanosecond laser ablation micro-pits on the substrate surface and high velocity oxygen fuel (HVOF) spraying WC coating to extend the erosion resistance of the valve. The characterization and evaluation of the erosion resistance of the WC-sprayed coating after the pretreatment of the 3Cr13 substrate surface polishing/grit blasting/nanosecond laser ablation circular micro-dimple were conducted using the unit coupon erosion test of liquid–solid two-phase flow, followed by the test evaluation and analysis of the erosion resistance test of the WC coating after different pretreatments of the full-size valve core. Results showed that the micro-dimple pretreatment on the surface of the 3Cr13 substrate increased the contact area rate and bonding strength of the substrate and the WC coating. By taking erosion volume loss as the evaluation index, the erosion resistance of the micro-dimple pretreatment on the surface of the 3Cr13 substrate was increased by about 31.98% compared with that of the polishing pretreatment. Therefore, the new method of surface nanosecond laser texture pretreatment and HVOF-spraying WC coating can effectively improve the erosion resistance of the valve.

Purpose: The purpose of this study is to investigate the influence of texture on hydrodynamic lubrication performance of slide surface from the perspective of skewness and kurtosis. Design/methodology/approach: Hydrodynamic lubrication theoretical model of textured surface was established based on two-dimensional Reynolds equation, and finite difference algorithm was used as the numerical approach in the paper. Skewness and kurtosis of surface were obtained by discrete calculation. Findings: Numerical analysis results show that the influence law of texture types on skewness, kurtosis and hydrodynamic lubrication was the more negative skewness and higher kurtosis, the better hydrodynamic lubrication performance when texture cross section contour and geometric parameters were the same. Similarly, the same influence law of skewness, kurtosis and hydrodynamic lubrication performance by texture cross-section contour was observed. However, it was unable to evaluate the effect of texture angle on hydrodynamic lubrication performance of textured surface from the perspective of skewness and kurtosis. Originality/value: This paper confirms the feasibility of evaluating influence of texture types and texture cross-section contour on hydrodynamic lubrication performance from the perspective of skewness and kurtosis and provides a way to optimize texture type and texture cross section.

Solid fluidization is a promising method for the development of marine hydrate resources. The back pressure makes it difficult to backfill the separated sand to the well bottom, resulting in a decrease in separation performance and serious failure of hydrocyclone. This study is intended to study the effect of underflow diameter on the performance of the hydrocyclone by computational fluid dynamics method. The results show that with the increase of back pressure, the split ratio basically decreases linearly, and the LAVV gradually increases. Under the same back pressure, the underflow diameter is larger, the pressure drop is smaller. No matter how large the underflow diameter is, the hydrocyclone may fail once back pressure exceeds 60 kPa. Under the same back pressure, the larger the underflow diameter is, the higher the desanding efficiency is, while the purification efficiency is opposite. When back pressure exceeds 60 kPa, the desanding efficiency drops sharply, while the purification efficiency remains basically unchanged. This study is applicable to downhole in-situ separation for solid fluidization of marine hydrate. The purpose of this study is to guide the structure design of hydrocyclone and the optimization of hydrate production process parameters.