Microbiologically induced CaCO₃ precipitation (MICP) is a well-known bio-based solution with application in environmental, geotechnical, and civil engineering. The significance of the MICP has increased explorations of process efficiency and specificity via natural bacterial isolates. In this study, comprehensive profiling of five soil ureolytic Bacillus strains was performed through a newly formed procedure that involved six steps from selection and identification, through kinetic study, to the characterization of the obtained precipitates, for the first time. To shorten the whole selection procedure of 43 bioagents with the MICP potential, Standard Score Analysis was performed and five selected bacteria were identified as Bacillus muralis, B. lentus, B. simplex, B. firmus, and B. licheniformis by the MALDI-TOF mass spectrometry. Despite following the targeted activity, kinetic studies were included important aspects of ureolysis and the MICP such as cell concentration, pH profiling, and reduction in calcium ion concentration. At the final step, characterization of the obtained precipitates was performed using FTIR, XRD, Raman, DTA/TGA, and SEM analysis. Although all tested strains showed significant potential in terms of precipitation of calcite or calcite and vaterite phase, the main differences in the MICP behavior can be observed at the bacterial strain level. B. licheniformis showed favorable behavior compared to the reference Sporosarcina pasteurii DSM 33.

Single-walled carbon nanotubes (SWCNTs) are well-known for their excellent electrical conductivity. One promising application for SWCNT-based thin films is as transparent electrodes for uncooled mid-IR detectors (MIR). In this paper, a combination of computational and experimental studies were performed to understand the chemistry behind the stability of carboxylic SWCNTs (SWCNTs-COOH) dispersions in different solvents. A computational study based on the density functional tight-binding (DFTB) method was applied to understand the interactions of COOH-functionalized carbon nanotubes with selected solvents. Attention was focused on understanding how the protonation of COOH groups influences the binding energies between SWCNTs and different solvents. Thin film electrodes were prepared by alternately depositing PEI and SWCNT-COOH on soda lime glass substrates. To prepare a stable SWCNT dispersion, different solvents were tested, such as deionized (DI) water, ethanol and acetone. The SWCNT-COOH dispersion stability was tested in different solvents. Samples were prepared to study the relationship between the number of depositions, transparency in the MIR range (2.5–5 µm) and conductivity, looking for the optimal thickness that would satisfy the application. The MIR transparency of the electrode was reduced by 20% for the thickest SWCNT layers, whereas sheet resistance values were reduced to 150–200 kΩ/sq.