The properties of carbides, such as morphology, size, and type, in H13 hot work die steel were studied with optical microscopy, transmission electron microscopy, electron diffraction, and energy dispersive X-ray analysis; their size distribution and quantity after tempering, at different positions within the ingot, were analyzed using Image-Pro Plus software. Thermodynamic calculations were also performed for these carbides. The microstructures near the ingot surface were homogeneous and had slender martensite laths. Two kinds of carbide precipitates have been detected in H13: (1) MC and M₆C, generally smaller than 200 nm; and (2) M₂₃C₆, usually larger than 200 nm. MC and M₆C play the key role in precipitation hardening. These are the most frequent carbides precipitating at the halfway point from the center of the ingot, and the least frequent at the surface. From the center of the ingot to its surface, the size and volume fraction of the carbides decrease, and the toughness improves, while the contribution of the carbides to the yield strength increases.

The mechanical properties, microstructures and precipitation behaviors in AISI (American Iron and Steel Institute) H13 steel tempered at 863 K for 0.5, 2, 4, 10 and 20 h were investigated. The values for H13 tempered for 2–4 h resulted in die steel that reached the desired properties as specified in NADCA (North American Die Casting Association) #207-2016. The cubic Ostwald ripening model was applied to simulate the coarsening of the large carbides, which were mainly M₂₃C₆ and M₃C, as determined from FactSage predictions as well as measurements with transmission electron microscopy (TEM). TEM revealed that the equivalent circle radius (ECR) decreased during 0.5–2 h, because of the nucleation of many new precipitates. According to the Ashby-Orowan modified precipitation strengthening model, this decrease in ECR leads to an increase in the contribution of precipitates to yield strength. Between 2 and 4 h tempering, the ECR of large carbides increases sharply but then increases asymptotically from 4 to 20 h, which obeys the calculated Ostwald ripening rate for cementite and M₂₃C₆ in H13 after 863 K tempering. This observation for the Ostwald ripening of M₂₃C₆ is in agreement with experimental data for other steels in the literature.