The microstructure and properties of Copper-Graphite Composites (CGC) prepared by spark plasma sintering (SPS) based on two-step mixing and wet milling were investigated. The results showed that Cu powders were rolled into Cu flakes during milling, and their size significantly decreased from 23.2 to 10.9 μm when the graphite content increased from 1.0 wt.% to 2.5 wt.%. The oxidation of Cu powder was avoided during two-step mixing and wet milling. After spark plasma sintering, the graphite powders of the composites were mainly distributed at Cu grain boundaries in granular and flake shapes. The mean size of Cu grains was 9.4 um for 1.0 wt.% graphite content and reduced slightly with the increasing of graphite content. Compared with other conventional methods, the composite prepared by two-step mixing and SPS achieved higher relative density, electrical conductivity, and micro-hardness, which, respectively, reduced from 98.78%, 89.7% IACS (International annealed copper standard), and 64 HV (Vickers-hardness) to 96.56%, 81.3% IACS, and 55 HV when the graphite content increased from 1.0 wt.% to 2.5 wt.%. As the graphite content increases, the friction coefficient and wear rate of the composite decreases. When the graphite content of CGC is 1.0 wt.%, the main wear mechanism was plastic deformation, delamination, adhesive, and fatigue wear. The adhesive and fatigue wear disappeared gradually with the increasing of graphite content.

The fabrication of porous copper with ultrahigh porosity by adding 90% spacer content was an unsolved technical problem in the field. In this study, the green compacts placed on a layer wire mesh during the decomposition process of needlelike carbamide as space holder with volume content up to 90% was successfully conducted to fabricate nondestructive porous copper. Compared with the green compacts directly placed on an alumina plate, the use of this support was crucial for manufacturing highly-porous copper. Characterization of macro- and microscopic morphologies as well as quasi-static compressive test for the obtained porous copper samples was carried out. The results show that the porosity of porous copper samples with 87.3% was slightly smaller than the spacer content. The SEM observation indicates that the internal pores of porous copper formed an open-cell structure and its skeleton was very dense. The compressive tests show that the stress–strain curve of a porous copper sample exhibits the typical characteristics of elastic-plastic metal foam. The energy absorption properties of porous copper samples were also comparable. This study provides a possibility for the preparation of porous copper and other metals with ultrahigh porosity by the well-known space holder method.