The design of hierarchical structures from biomass has become one of the hottest subjects in the field of microwave absorption due to its low cost, vast availability and sustainability. A kapok-fiber-derived carbon microtube was prepared by facile carbonization, and the relation between the structure and properties of the carbonized kapok fiber (CKF) was systematically investigated. The hollow tubular structures afford the resulting CKF composites with excellent microwave-absorbing performance. The sample with a 30 wt.% loading of CKF in paraffin demonstrates the strongest microwave attenuation capacity, with a minimum reflection loss of −49.46 dB at 16.48 GHz and 2.3 mm, and an optimized effective absorption bandwidth of 7.12 GHz (10.64–17.76 GHz, 2.3 mm) that covers 34% of the X-band and 96% of the Ku-band. Further, more than 90% of the incident electromagnetic wave in the frequency from 4.48 GHz to 18.00 GHz can be attenuated via tuning the thickness of the CKF-based absorber. This study outlines a foundation for the development of lightweight and sustainable microwave absorbers with a high absorption capacity and broad effective absorption bandwidth.

IAN873, Dongfang93114 and Reyan73397, created through vegetative propagation for their high yield and excellent cold resistance, are major clones planted in China. In this work, latexes with rubber particles of the same size from these clones are separated from fresh natural rubber latex, and corresponding rubber films are prepared from each latex. The structure and components of each film are measured. This indicates that the characteristics of the rubbers obtained from latexes with similar particle sizes show some resembling trends among different clones, while for specific samples, those characteristics vary depending on the clone. The molecular weight is generally highest in IAN873 and lowest in Reyan73397. Rubber chains in small rubber particles are longer, and large rubber particles show a wider molecular weight distribution. The gel content of every sample from Reyan73397 is lower than the other two clones. The nitrogen content increases with the size of rubber particles in all clones. The ester content of small rubber particles in IAN873 and Reyan73397 is almost zero. Large rubber particles have more branching points formed via esters. This study provides a new perspective on the influence of clones on the relationship between characteristics of natural rubber and the size of rubber particles in natural rubber latex.

Constructing hierarchical structures is indispensable to tuning the electromagnetic properties of carbon-based materials. Here, carbon microtubes with nanometer wall thickness and micrometer diameter were fabricated by a feasible approach with economical and sustainable kapok fiber. The carbonized kapok fiber (CKF) exhibits microscale pores from the inherent porous templates as well as pyrolysis-induced nanopores inside the wall, affording the hierarchical carbon microtube with excellent microwave absorbing performance over broad frequency. Particularly, CKF-650 exhibits an optimized reflection loss (RL) of −62.46 dB (10.32 GHz, 2.2 mm), while CKF-600 demonstrates an effective absorption bandwidth (RL < −10 dB) of 6.80 GHz (11.20–18.00 GHz, 2.8 mm). Moreover, more than 90% of the incident electromagnetic wave ranging from 2.88 GHz to 18.00 GHz can be dissipated by simply controlling the carbonization temperature of KF and/or the thickness of the carbon-microtube-based absorber. These encouraging findings provide a facile alternative route to fabricate microwave absorbers with broadband attenuation capacity by utilizing sustainable biomass.