Bioprinting of body tissues has gained great attention in recent years due to its unique advantages, including the creation of complex geometries and printing the patient-specific tissues with various drug and cell types. The most momentous part of the bioprinting process is bioink, defining as a mixture of living cells and biomaterials (especially hydrogels). Among different biomaterials, natural polymers are the best choices for hydrogel-based bioinks due to their intrinsic biocompatibility and minimal inflammatory response in body condition. Gelatin methacryloyl (GelMA) hydrogel is one of the high-potential hydrogel-based bioinks due to its easy synthesis with low cost, great biocompatibility, transparent structure that is useful for cell monitoring, photocrosslinkability, and cell viability. Furthermore, the potential of adjusting properties of GelMA due to the synthesis protocol makes it a suitable choice for soft or hard tissues. In this review, different methods for the bioprinting of GelMA-based bioinks, as well as various effective process parameters, are reviewed. Also, several solutions for challenges in the printing of GelMA-based bioinks are discussed, and applications of GelMA-based bioprinted tissues argued as well.

Despite the significant advancement in bone tissue engineering, it is still challenging to find a desired scaffold with suitable mechanical and biological properties, efficient bone formation in the defect area, and antibacterial resistivity. In this study, the zeolite (ZSM-5) scaffold was developed using the space holder method, and a novel vancomycin-loaded alginate coating was developed on it to promote their characteristics. Our results demonstrated the importance of alginate coating on the microstructure, mechanical, and cellular properties of the ZSM-5 scaffold. For instance, a three-fold increase in the compressive strength of coated scaffolds was observed compared to the uncoated ZSM-5. After the incorporation of vancomycin into the alginate coating, the scaffold revealed significant antibacterial activity against Staphylococcus aureus (S. aureus). The inhibition zone increased to 35 mm. Resets also demonstrated 74 ± 2.5% porosity, 4.3 ± 0.07 MPa strength in compressive conditions, acceptable cellular properties (72.3 ± 0.2 (%control) cell viability) after 7 days, good cell attachment, and calcium deposition. Overall, the results revealed that this scaffold could be a great candidate for bone tissue engineering.