We explore a phase engineering strategy to improve the electrochemical performance of transition metal sulfides (TMSs) in anode materials for lithium-ion batteries (LIBs). A one-pot hydrothermal approach has been employed to synthesize MoS₂ nanostructures. MoS₂ and MoO₃ phases can be readily controlled by straightforward calcination in the (200–300) °C temperature range. An optimized temperature of 250 °C yields a phase-engineered MoO₃@MoS₂ hybrid, while 200 and 300 °C produce single MoS₂ and MoO₃ phases. When tested in LIBs anode, the optimized MoO₃@MoS₂ hybrid outperforms the pristine MoS₂ and MoO₃ counterparts. With above 99% Coulombic efficiency (CE), the hybrid anode retains its capacity of 564 mAh g⁻¹ after 100 cycles, and maintains a capacity of 278 mAh g⁻¹ at 700 mA g⁻¹ current density. These favorable characteristics are attributed to the formation of MoO₃ passivation surface layer on MoS₂ and reactive interfaces between the two phases, which facilitate the Li-ion insertion/extraction, successively improving MoO₃@MoS₂ anode performance.

Metal-assisted chemical etching (MACE) is widely used to fabricate micro-/nano-structured Si owing to its simplicity and cost-effectiveness. The technique of magnetically guided MACE, involving MACE with a tri-layer metal catalyst, was developed to improve etching speed as well as to adjust the etching direction using an external magnetic field. However, the controllability of the etching direction diminishes with an increase in the etching dimension, owing to the corrosion of Fe due to the etching solution; this impedes the wider application of this approach for the fabrication of complex micro Si structures. In this study, we modified a tri-layer metal catalyst (Au/Fe/Au), wherein the Fe layer was encapsulated to improve direction controllability; this improved controllability was achieved by protecting Fe against the corrosion caused by the etching solution. We demonstrated curved Si microgroove arrays via magnetically guided MACE with Fe encapsulated in the tri-layer catalyst. Furthermore, the curvature in the curved Si microarrays could be modulated via an external magnetic field, indicating that direction controllability could be maintained even for the magnetically guided MACE of bulk Si. The proposed fabrication method developed for producing curved Si microgroove arrays can be applied to electronic devices and micro-electromechanical systems.