Switchgrass was pretreated with sodium hydroxide (NaOH) at various concentrations and pretreatment times to investigate how delignification caused by NaOH affects its lignin chemistry. NaOH resulted in significant delignification ranging from 44.0 to 84.6% depending on pretreatment intensity. While there was no significant glucan loss due to NaOH pretreatment, higher NaOH concentrations removed xylan by up to 28.3%. Nitrobenzene oxidation (NBO) was used to study changes in lignin chemistry, and indicated that at higher NaOH concentrations, the amount of 4-hydroxygenzaldehyde (Hy) degraded from p-hydroxyphenyl propanol (H) lignin units was significantly reduced (p < 0.05). However, amounts of syringic (SA) and vanillic (VA) acids generated from syringyl (S) and guaiacyl (G) degradation were greater at higher NaOH concentration. S/G ratio (=0.62 raw switchgrass) did not significantly (p > 0.05) change with 15 min pretreatment, but it increased to 0.75 and 0.72, respectively, with 30 and 60 min pretreatments (p < 0.05). Increase in NaOH concentration did not significantly (p > 0.05) change S/G ratio, but H/G ratio (=0.48 raw switchgrass) decreased significantly to 0.14 regardless of pretreatment times. Overall, the H unit was found to be more susceptible to NaOH than S and G unit monolignols. Though changes in lignin chemistry due to NaOH concentration were observed, their impact on cellulolytic enzyme action during hydrolysis could not be fully understood. Further studies on lignin isolation may help to determine how these changes in lignin chemistry by NaOH impact cellulolytic enzymes.

There is a significant interest in using agricultural wastes such as rice husk as a precursor for the synthesis of adsorbents and catalysts. In this article, readers will find valuable baseline characterization data related to physical and chemical properties of raw rice husk including BET specific surface area, acid value, the point of zero charge, elemental analysis, Time-of-Flight Secondary Ion Mass Spectrometric Analysis X-Ray Photoelectron Spectroscopic Analysis, and Scanning Electron Microscope-Energy Dispersive Spectroscopic Analysis. It is expected that the baseline raw data presented in this article will be useful for researchers around the world who are working on chemically modifying rice husk for valorizing them for applications in adsorption, catalysis, and energy storage.