Rheological parameters of cellulose nanofibril dispersions (CNF) are relevant and commonly used as quality control for producing of this type of material. These parameters are affected by morphological features and size distribution of the nanofibrils. Understanding the effect of size distribution is essential for analyzing the rheological properties, viscosity control, performance of CNFs, and potential dispersion applications. This study aims at comprehending how the morphological characteristics of the CNFs and their size distribution affect the rheological behavior of dispersions. The CNF dispersions were fractionated by size, obtaining six fractions of each, which were analyzed for their morphology and rheology (viscosity, intrinsic viscosity). In the dilute region, the viscosity and intrinsic viscosity behavior of CNF dispersions are linear concerning the size distribution present in the dispersion. In the semi-dilute region, the size of the fibrils and the fiber aggregates have a relevant effect on the viscosity behavior of CNF dispersions, which are satisfactorily related (R² = 0.997) using the rule of logarithmic additivity of the dispersion viscosities of size fractions.

The available research does not allow specific relationships to be established between the applied enzymatic-mechanical treatment, the degree of polymerization, and the characteristics of the cellulose nanofibrils (CNFs) produced. This work aims to establish specific relationships between the intensity of enzymatic treatment, the degree of polymerization of the cellulose, the morphology of CNFs, and the tensile strength of the CNF films. It is determined that the decrease in the degree of polymerization plays an essential role in the fibrillation processes of the cell wall to produce CNFs and that there is a linear relationship between the degree of polymerization and the length of CNFs, which is independent of the type of enzyme, enzyme charge, and intensity of the applied mechanical treatment. In addition, it is determined that the percentage of the decrease in the degree of polymerization of CNFs due to mechanical treatment is irrespective of the applied enzyme charge. Finally, it is shown that the aspect ratio is a good indicator of the efficiency of the fibrillation process, and is directly related to the mechanical properties of CNF films.

This study analyzes the effect of different drying methods on the surface properties of cellulose nanofibril (CNF) films obtained from bleached eucalyptus Kraft pulp. The surface quality of CNF films is crucial for enhancing their barrier properties, adhesion, and uniformity, particularly in multilayer or composite applications. Films were fabricated by casting, hot pressing, and double pressing under various conditions of pressure and temperature. Surface roughness, morphology, density, porosity, and contact angle were evaluated. The most effective method was double pressing in an oven at 110 °C and 1.8 kPa, achieving the lowest roughness (283.8 nm), highest density (1.34 g/cm³), low porosity (16.1%), and a contact angle of 63.1°, indicating a more compact and less hydrophilic surface. This study establishes a rapid and efficient method to produce CNF films with optimized surface properties, which are highly relevant for industrial applications in sustainable packaging, coatings, and barrier materials, where surface quality directly impacts functionality and competitiveness.

Chile is among the leading global exporters of pulp and paper, supported by extensive plantations of Pinus radiata and Eucalyptus spp. This review synthesizes recent progress in the valorization of forestry biomass in Chile, including both established practices and emerging bio-based applications. It highlights advances in lignin utilization, nanocellulose production, hemicellulose processing, and tannin extraction, as well as developments in thermochemical conversion technologies, including torrefaction, pyrolysis, and gasification. Special attention is given to non-timber forest products and essential oils due to their potential bioactivity. Sustainability perspectives, including Life Cycle Assessments, national policy instruments such as the Circular Economy Roadmap and Extended Producer Responsibility (REP) Law, are integrated to provide context. Barriers to technology transfer and industrial implementation are also discussed. This work contributes to understanding how forestry biomass can support Chile’s transition toward a circular bioeconomy.