A 3D printing was successfully used to fabricate samples of Polylactic Acid (PLA). Processing parameters such as Lay-up speed, Lay-up thickness, and printing nozzle were varied. All samples were tested for flexural strength using three point load test. A statistical mathematical model was developed to correlate the processing parameters with flexural strength. The result clearly demonstrated that the lay-up thickness and nozzle diameter influenced flexural strength significantly, whereas lay-up speed hardly influenced the flexural strength.