Intimate coupling of photocatalysis and biodegradation (ICPB) has shown promise in removing unwanted organic compounds from water. In this study, bagasse cellulose titanium dioxide composite carrier (SBC-TiO₂) was prepared by low-temperature foaming methods. The optimum preparation conditions, material characterization and photocatalytic performance of the composite carrier were then explored. By conducting a single factor test, we found that bagasse cellulose with a mass fraction of 4%, a polyvinyl alcohol solution (PVA) with a mass fraction of 5% and 20 g of a pore-forming agent were optimum conditions for the composite carrier. Under these conditions, good wet density, porosity, water absorption and retention could be realized. Scanning electron microscopy (SEM) results showed that the composite carrier exhibited good biologic adhesion. X-ray spectroscopy (EDS) results confirmed the successful incorporation of nano-TiO₂ dioxide into the composite carrier. When the mass concentration of methylene blue (MB) was 10 mg L⁻¹ at 200 mL, 2 g of the composite carrier was added and the initial pH value of the reaction was maintained at 6, the catalytic effect was best under these conditions and the degradation rate reached 78.91% after 6 h. The method of preparing the composite carrier can aid in the degradation of hard-to-degrade organic compounds via ICPB. These results provide a solid platform for technical research and development in the field of wastewater treatment.

Chrysin is a natural bioactive molecule with various groups, and it has been a challenge to separate and enrich chrysin from natural products. Molecularly imprinted polymers have been widely used in the extraction of natural products, but the number and type of functional monomers limits the separation effect. The synergistic action of multiple functional monomers can improve the separation effect. In this paper, molecularly imprinted polymers (Bi-MIPs) were prepared using methacrylic acid and acrylamide as binary functional monomers for the separation and enrichment of chrysin. The Bi-MIPs were characterized using thermogravimetric analyzer (TGA), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscope (SEM). The performances of Bi-MIPs were assessed, which included adsorption isotherms, selective recognition and adsorption kinetics. The experimental results show that Bi-MIPs are shaped as a uniform sphere with an abundant pocket structure on its surface. The adsorption of chrysin on the Bi-MIPs followed a pseudo-second-order and adapted Langmuir–Freundlich isotherm models. The adsorption performance of the Bi-MIPs was determined at different temperatures, and the Bi-MIPs showed excellent adsorption performance at 30 °C. The initial decomposition temperature of the Bi-MIPs was 220 °C. After five times of adsorption and desorption, the adsorption performance of the Bi-MIPs decreased by only 7%. In contrast with single functional monomer molecularly imprinted polymers (Si-MIPs), the Bi-MIPs showed excellent specificity, with an imprinting factor of 1.54. The Bi-MIPs are promising materials in the separation and enrichment of chrysin for their high adsorption capacity, low cost and being environmentally friendly.

Intimate coupling photocatalysis and biodegradation treatment technology is an emerging technology in the treatment of refractory organic matter, and the carrier plays an important role in this technology. In this paper, sugarcane cellulose was used as the basic skeleton, absorbent cotton was used as a reinforcing agent, anhydrous sodium sulfate was used as a pore-forming agent to prepare a cellulose porous support with good photocatalytic performance, and nano-TiO₂ was loaded onto it by a low-temperature bonding method. The results showed that the optimal preparation conditions of cellulose carriers were: cellulose mass fraction 1.0%; absorbent cotton 0.6 g; and Na₂SO₄ 60 g. The SEM, EDS and XPS characterization further indicated that the nano-TiO₂ was uniformly loaded onto the cellulose support. The degradation experiments of Rhodamine B showed that the nano-TiO₂-loaded composite supports had good photocatalytic performance. The degradation rate of 1,2,4-trichlorobenzene was more than 92% after 6 cycles, and the experiment of adhering a large number of microorganisms on the carriers before and after the reaction showed that the cellulose-based carriers obtained the required photocatalytic performance and stability, which is a good cellulose porous carrier.