Additive manufacturing (AM) is a rapidly growing field of technology. In order to increase the variety of metal alloys applicable for AM, selective laser melting (SLM) of duplex stainless steel 2205 powder and the resulting microstructure, density, mechanical properties, and corrosion resistance were investigated. An optimal set of processing parameters for producing high density (>99.9%) material was established. Various post-processing heat treatments were applied on the as-built predominantly ferritic material to achieve the desired dual-phase microstructure. Effects of annealing at temperatures of 950 °C, 1000 °C, 1050 °C, and 1100 °C on microstructure, crystallographic texture, and phase balance were examined. As a result of annealing, 40–46 vol.% of austenite phase was formed. Annealing decreased the high yield and tensile strength values of the as-built material, but significantly increased the ductility. Annealing also decreased the residual stresses in the material. Mechanical properties of the SLM-processed and heat-treated materials outperformed those of conventionally produced alloy counterparts. Using a scanning strategy with 66° rotation between layers decreased the strength of the crystallographic texture. Electrochemical cyclic potentiodynamic polarization testing in 0.6 M NaCl solution at room temperature showed that the heat treatment improved the pitting corrosion resistance of the as-built SLM-processed material.

Dissimilar metal welds (DMWs) are a key design feature in nuclear power systems, typically involving ferritic low-alloy steels (LAS), stainless steels (SS), and nickel-base alloys. They are, however, a potential concern regarding the structural integrity of nuclear power systems. In particular, the LAS/nickel-base alloy weld metal interface is known to develop a local strength mismatch upon post-weld heat treatment (PWHT). Very limited data is available on the effect of thermal ageing on the DMW interface. The aim of this study was to investigate the effects of thermal ageing at 400 °C for up to 10,000 h on a narrow-gap DMW mock-up representative of the weld between the reactor pressure vessel nozzle and its safe-end after PWHT, with a special focus on the LAS SA 508/nickel-base Alloy 52 weld metal interface. No significant effect of thermal ageing on the appearing microstructure was observed in either LAS base material, LAS heat-affected zone or Alloy 52 weld metal. However, thermal ageing reduced the local strength mismatch at the LAS/nickel-base weld metal interface formed during PWHT. The reduction of the strength mismatch was detected using nanoindentation measurements and was concluded to be associated with a decrease in the carbon pile-up in the weld metal caused by PWHT. Based on the obtained results, thermal ageing promotes carbon diffusion from the weld metal side of the fusion boundary further away into the weld metal and thus slightly decreases the local strength mismatch.

Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and constant load tensile testing, the studied materials seem not to be particularly susceptible to delayed cracking. Delayed cracks were only occasionally initiated in two of the materials at high local stress levels. However, if a delayed crack initiated in a highly stressed location, strain-induced martensite transformation decreased the crack arrest tendency of the austenite phase in a duplex microstructure. According to electron microscopy examination and electron backscattering diffraction analysis, the fracture mode was predominantly cleavage, and cracks propagated along the body-centered cubic (BCC) phases ferrite and α’-martensite. The BCC crystal structure enables fast diffusion of hydrogen to the crack tip area. No delayed cracking was observed in the stainless steel that had high austenite stability. Thus, it can be concluded that the presence of α’-martensite increases the hydrogen-induced cracking susceptibility.

The role of the excessive metal vacancy generation in transgranular stress corrosion cracking (TGSCC) of pure copper was studied in relation to crack initiation and growth mechanisms. Electrochemically polarized specimens were strained at room temperature in 0.3 m NaNO ₂ solution. Cation vacancy redistribution under applied anodic polarization took place at the p-n junction of the duplex Cu ₂ O oxide film, resulting in cation vacancy transport in the p-type layer of the oxide to the metal substrate interface and in excessive metal vacancy accumulation in the metal substrate. The rapid initiation of TGSCC at room temperature in the cold-worked oxygen-free high-conductivity copper samples occurred during slow strain rate tests under anodic polarization in 0.3 m NaNO ₂ solution. The duplex Cu ₂ O oxide film structure formed by cathodic deposition, before applying the anodic polarization, was characterized with X-ray diffraction and field emission scanning electron microscopy/electron backscatter diffraction/energy-dispersive spectroscopy. The redistribution of cation vacancies in the p-type oxide phase due to the anodic polarization and the metal vacancy accumulation in the copper substrate interface was studied by using positron annihilation spectroscopy.