The significant difference between recycled aggregate and natural aggregate is the content of the attached mortar layer. With the increase of the replacement rate of recycled aggregate, the shrinkage and creep of recycled aggregate concrete is significantly increased. In this paper, 180-day shrinkage and creep tests of recycled aggregate concrete with different water–cement ratios were designed in order to analyze the effect of the substitution rate and water–cement ratio on shrinkage and creep properties. The results show that the shrinkage strain of recycled aggregate concrete with a substitution rate of 50% and 100% at 180 days is 26% and 48% higher than that of ordinary concrete, respectively, and the growth of group II is 22% and 47%, respectively. When the load was 180 days old, the creep coefficient of recycled aggregate concrete with a substitution rate of 50% and 100% in group I increased by 19.6% and 39.6%, respectively compared with ordinary concrete, and group II increased by 23.6% and 44.3%, respectively. Based on the difference of adhering mortar content, the creeping increase coefficient and shrinkage increase coefficient of the attached mortar were proposed, and a shrinkage and creep model of recycled aggregate concrete was established. When compared with the experimental results, the model calculation results met the accuracy requirements.

In this paper, the compressive strength experiment for three groups of recycled aggregate concrete (RAC) specimens with different replacement ratios of recycled aggregate (0%, 50%, 100%) was carried out. The mechanism of the block and mortar properties on the compressive strength of block masonry was investigated by means of a static loading test. The formula for calculating the compressive strength of a recycled concrete block was obtained based on experimental data. Moreover, the global warming potential (GWP) of recycled aggregate concrete (RAC) block masonry was evaluated by life cycle assessment (LCA) methodology. The feasibility for application of RAC block masonry was discussed combined with environmental impact data analysis. The results show that the strength of RAC blocks is the principal element affecting the compressive strength of block masonry, and the strength of mortar also has a certain impact for the compressive of RAC block masonry; the sub-coefficient of material performance should be enhancive appropriately for ensuring the construction quality of RAC block masonry; the total GWP of RAC block is lower than that of natural aggregate concrete (NAC) block. The environmental benefits of the promotion and application of RAC block masonry are inspiring.

We doubt whether the monolithic precast concrete structure could be designed as the cast‐in‐place structure in high seismic intensity area. To solve the puzzle, the 1/5 scaled monolithic precast concrete structure model and cast‐in‐place structure model were designed and tested by shake table. Comparative analysis between them was made to better understand their seismic behavior. Based on the experimental results, the failure pattern and mechanism were different, which was concentrated damage in coupling beam and then extended to shear walls of CIPS, and the weak connections presented cracks between precast elements besides the damage coupling beam of MPCS. The natural frequency of MPCS possessed a typical feature for the weakness of connections, which was the initial one greater than that of CIPS and decreased fast after the first waves with PGA of 0.035 g. Acceleration amplifying factors presented variation trend under the different earthquake waves. The distribution of seismic response presented linearity along the height of models in plastic stage and turned into nonlinearity later for severe damage. In general, the MPCS and CIPS had similar seismic responses, except typical characteristics. And they were proven to have better seismic performance without collapse under the high‐intensity earthquake waves.

This paper aims to manufacture recycled concrete hollow block (RCHB) which can be used for the masonry structure with seismic requirements. Five RCHB masonry walls were tested under cyclic loading to evaluate the effect of the axial compression stress, aspect ratio, and the materials of structural columns on the seismic performance. Based on the test results, the failure pattern, hysteresis curves, lateral drift, ductility, stiffness degradation, and the energy dissipation of the specimens were analyzed in detail. The results showed that with the increase of aspect ratios, the ductility of RCHB masonry walls increased, but the horizontal bearing capacity and energy dissipation of RCHB masonry walls decreased. With the increase of compressive stress, the bearing capacity and energy dissipation performance of RCHB masonry walls were improved, and the stiffness degraded slowly. The results also demonstrated that the RCHB masonry walls with structural columns, depending on whether the structural columns were prepared by ordinary concrete or recycled concrete, could increase the bearing capacity, ductility, and energy dissipation of specimens. The research confirmed that RCHB masonry walls could meet the seismic requirements through thoughtful design. Therefore, this study provided a new cleaner production for the utilization of construction waste resources.