Through atomistic simulations, this work investigated the permeability of hexagonal diamond nanochannels for NaCl solution. Compared with the multilayer graphene nanochannel (with a nominal channel height of 6.8 Å), the diamond nanochannel exhibited better permeability. The whole transportation process can be divided into three stages: the diffusion stage, the transition stage and the flow stage. Increasing the channel height reduced the transition nominal pressure that distinguishes the diffusion and flow stages, and improved water permeability (with increased water flux but reduced ion retention rate). In comparison, channel length and solution concentration exerted ignorable influence on water permeability of the channel. Further simulations revealed that temperature between 300 and 350 K remarkably increased water permeability, accompanied by continuously decreasing transition nominal pressure. Additional investigations showed that the permeability of the nanochannel could be effectively tailored by surface functionalization. This work provides a comprehensive atomic insight into the transportation process of NaCl solution in a diamond nanochannel, and the established understanding could be beneficial for the design of advanced nanofluidic devices.

Metallic nanowires (NWs) are essential building blocks for flexible electronics, and experience different deformation modes due to external mechanical loading. Using atomistic simulations, this work investigated the deformation behavior of copper nanowire under coupled tension–torsion loading. A transition in both yielding pattern and dislocation pattern were observed with varying torsion/tension strain ratios. Specifically, increasing the torsion/tension strain ratio (with larger torsional strain) triggered the nucleation of different partial dislocations in the slip system. At low torsion/tension strain ratios, plastic deformation of the nanowire was dominated by stacking faults with trailing partial dislocations pinned at the surface, shifting to two partial dislocations with stacking faults as the strain ratio increases. More interestingly, the NW under tension-dominated loading exhibited a stacking fault structure after yielding, whereas torsion-dominated loading resulted in a three-dimensional dislocation network within the structure. This work thus suggests that the deformation behavior of the NW varies depending on the coupled mechanical loading, which could be beneficial for various engineering applications.