Spinel-type ZnMn₂O₄ nanoparticles were synthesized via a simple and inexpensive microwave-assisted colloidal route. Structural studies by X-ray diffraction showed that a spinel crystal phase of ZnMn₂O₄ was obtained at a calcination temperature of 500 °C, which was confirmed by Raman and UV-vis characterizations. Spinel-type ZnMn₂O₄ nanoparticles with a size of 41 nm were identified by transmission electron microscopy. Pellet-type sensors were fabricated using ZnMn₂O₄ nanoparticles as sensing material. Sensing measurements were performed by exposing the sensor to different concentrations of propane or carbon monoxide at temperatures in the range from 100 to 300 °C. Measurements performed at an operating temperature of 300 °C revealed a good response to 500 ppm of propane and 300 ppm of carbon monoxide. Hence, ZnMn₂O₄ nanoparticles possess a promising potential in the gas sensors field.

Spinel ZnCo₂O₄ nanoparticles were synthesized by means of the microwave-assisted colloidal method. A solution containing ethanol, Co-nitrate, Zn-nitrate, and dodecylamine was stirred for 24 h and evaporated by a microwave oven. The resulting solid material was dried at 200 °C and subsequently calcined at 500 °C for 5 h. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and Raman spectroscopy, confirming the formation of spinel ZnCo₂O₄ nanoparticles with average sizes between 49 and 75 nm. It was found that the average particle size decreased when the dodecylamine concentration increased. Pellets containing ZnCo₂O₄ nanoparticles were fabricated and tested as sensors in carbon monoxide (CO) and propane (C₃H₈) gases at different concentrations and temperatures. Sensor performance tests revealed an extremely high response to 300 ppm of CO at an operating temperature of 200 °C.

In this research, we are reporting the treatment of tequila vinasse by a coagulation–flocculation process coupled with heterogeneous photocatalysis using two types of titanium dioxide nanoparticles, i.e. (1) commercial nanoparticles, and (2) nanoparticles synthesized by sol–gel. The efficiency in the elimination of phenol, which is one of the most harmful contaminants in tequila vinasse, was also included in the evaluation of the treatment process. The synthesized titanium dioxide nanoparticles were annealed in air at 400°C for 1 h and were characterized by X-ray diffraction, transmission electron microscopy, ultraviolet-visible and Raman spectroscopy. Anatase phase was observed in both samples, with a crystallite size of 22.5 and 9.8 nm for commercial and synthesized nanoparticles respectively. Tequila vinasse was characterized before and after the treatments by measuring physicochemical parameters such as pH, chemical oxygen demand (COD), colour, total suspended solids (TSS), as well as using ultraviolet-visible spectroscopy and Raman spectroscopy to identify the presence of organic compounds, and gas chromatography (GC) for phenol quantification. Raw vinasse was treated initially by coagulation–flocculation producing clarified vinasse, which in turn was treated by photocatalysis for 3 h using hydrogen peroxide as oxidizing agent. The use of synthesized titanium dioxide nanoparticles allowed the highest efficiencies, reaching reductions of 99.4%, 86.0%, and 70.0% for TSS, colour, and COD respectively. GC results showed the reduction of phenol concentrations in 89.7% with our synthesized nanoparticles in contrast to 82.7% reduction, with commercial titanium dioxide nanoparticles. GRAPHICAL ABSTRACT

Micro- and nanoparticles of NiSb₂O₆ were synthesized by the microwave-assisted colloidal method. Nickel nitrate, antimony chloride, ethylenediamine, and ethyl alcohol were used. The oxide was obtained at 600°C and was analyzed by X-ray diffraction (XRD) and Raman spectroscopy, showing a trirutile-type structure with cell parameters a = 4.641 Å, c = 9.223 Å, and a space group P4₂/mnm (136). Average crystal size was estimated at ~31.19 nm, according to the XRD-peaks. The microstructure was scrutinized by scanning electron microscopy (SEM), observing microrods measuring ~3.32 μm long and ~2.71 μm wide, and microspheres with an average diameter of ~8 μm; the size of the particles shaping the microspheres was measured in the range of ~0.22 to 1.8 μm. Transmission electron microscopy (TEM) revealed that nanoparticles were obtained with sizes in the range of 2 to 20 nm (~10.7 nm on average). Pellets made of oxide’s powders were tested in propane (C₃H₈) and carbon monoxide (CO) atmospheres at different concentrations and temperatures. The response of the material increased significantly as the temperature and the concentration of the test gases rose. These results show that NiSb₂O₆ may be a good candidate for gas sensing applications.