A new approach is presented for analysis of microplastics in environmental samples, based on selective fluorescent staining using Nile Red (NR), followed by density-based extraction and filtration. The dye adsorbs onto plastic surfaces and renders them fluorescent when irradiated with blue light. Fluorescence emission is detected using simple photography through an orange filter. Image-analysis allows fluorescent particles to be identified and counted. Magnified images can be recorded and tiled to cover the whole filter area, allowing particles down to a few micrometres to be detected. The solvatochromic nature of Nile Red also offers the possibility of plastic categorisation based on surface polarity characteristics of identified particles. This article details the development of this staining method and its initial cross-validation by comparison with infrared (IR) microscopy. Microplastics of different sizes could be detected and counted in marine sediment samples. The fluorescence staining identified the same particles as those found by scanning a filter area with IR-microscopy.

Graphene and its derivatives have become the most explored materials since Novoselov and Geim (Nobel Prize winners for Physics in 2010) achieved its isolation in 2004. The exceptional properties of graphene have attracted the attention of the scientific community from different research fields, generating high impact not only in scientific journals, but also in general-interest newspapers. Optical fibre sensing is one of the many fields that can benefit from the use of these new materials, combining the amazing morphological, chemical, optical and electrical features of graphene with the advantages that optical fibre offers over other sensing strategies. In this document, a review of the current state of the art for optical fibre sensors based on graphene materials is presented.

To inform risk assessments, reliable, time efficient and affordable quantification methods are required for creating a microplastic (MP) pollution baseline in the world's oceans. To facilitate this, MP abundance was investigated in sediments of three contrasting areas of the UK continental shelf: North West of Jones Bank, the Canyons in the Celtic Sea and Dogger Bank in the North Sea, utilising the Nile Red tagging method to assess its time efficiency and cost. Average MP abundance in the top 10 cm was 1050-2700 MP kg^-1. MP abundance decreased with increasing sediment depth and increased with increasing water depth. The findings emphasise the extent of MP pollution and illustrate the value of Nile Red for large scale mapping at relatively low cost.

Poly(styrene) (PS) has been heavily utilised in disposable food packaging due to its insulating properties, optical translucency, and long-shelf life. Despite these desirable characteristics, (PS) poses toxicity concerns to human’s health through styrene monomer leaching into foodstuffs. Environmental and marine hazards are another growing concerns due to improper and/or absence of recycling strategies and facilities. This preliminary work aims to investigate the effect of temperature, food composition and contact times on the migration of the styrene monomer from poly(styrene) food contact materials into food simulants. Poly(styrene) cups showed a relatively low level of styrene migration with the highest being 0.110 µg/mL, whereas food containers showed a much higher level of styrene leaching with up to 6 µg/mL. This could be due to an increase in the hydrophobicity of the simulants’ characteristics from low to high fat content and the increase in the testing temperatures from 5 °C to 70 °C. ANOVA statistical analysis is used to compare the means of three or more groups of data, whereas t-test analysis is used to compare means of two groups. This was carried out on each individual sample to determine the significance of changing the temperature, simulant type, or both on the level of migration observed in the results. All significant values were tested at 95% confidence level p < 0.05, concluding that fat content and high temperatures were found to significantly increase the level of styrene migration. Nile Red staining method was used to demonstrate that particulate poly(styrene), as well as styrene monomer, migrated into tested food simulants from typical containers, which is becoming a cause for concern as evidence of microplastic ingestion increases.