In an industrial joining process, exemplified by deep penetration laser beam welding, ensuring a high quality of welds requires a great effort. The quality cannot be fully established by testing, but can only be produced. The fundamental requirements for a high weld seam quality in laser beam welding are therefore already laid in the process, which makes the use of control systems essential in fully automated production. With the aid of process monitoring systems that can supply data inline to a production process, the foundation is laid for the efficient and cycle-time-neutral control of welding processes. In particular, if novel, direct measurement methods, such as Optical Coherence Tomography, are used for the acquisition of direct geometric quantities, e.g., the weld penetration depth, a significant control potential can be exploited. In this work, an inline weld depth control system based on an OCT keyhole depth measurement is presented. The system is capable of automatically executing an inline control of the deep penetration welding process based only on a specified target weld depth. The performance of the control system was demonstrated on various aluminum alloys and for different penetration depths. In addition, the ability of the control to respond to unforeseen external disturbances was tested. Within the scope of this work, it was thus possible to provide an outlook on future developments in the field of laser welding technology, which could develop in the direction of an intuitive manufacturing process. This objective should be accomplished through the use of intelligent algorithms and innovative measurement technology—following the example of laser beam cutting, where the processing systems themselves have been provided with the ability to select suitable process parameters for several years now.

Compound casting is a process in which a single component is made from two metallic materials, such as aluminum and steel. Solid-liquid bimetallic compounds can be produced by suitable process control. This technology can reduce the number of joining processes, and the specific properties of the respective metal component can be used for specifically designed product properties, for example, where lightweight and high strength are needed. This paper presents an experimental methodology for producing a purely material-bonded bimetallic joint from cast aluminum and zinc-coated sheet steel in 3D sand casting using an inductive heating system. The process-related temperature characterisation in the compound zone is described using a heating test rig and temperature measurements. It shows that inductive preheating can only produce a material bond between the aluminum casting and the coated steel sheet. Shear tensile tests showed strengths between 15 MPa and 22 MPa. Laser surface pre-treatment using laser ablation cutting on the coated steel sheet was carried out to investigate the benefit of possible microform-locking. The results show a strength-reducing influence on the tensile shear tests. Micrographs showed the formation of Al_4.5FeSi and Al₇Fe₂Si, as well as the formation of other undefined intermetallic phases. The thickness of the compound zone is 10 µm.