Red mud storage is associated with an increased risk of dam failure and there is an urgent need to address the environmental problem caused by the very fine particle size (average 4.9 µm) of red mud with high alkalinity (pH = 10–12.5) in the alumina industry. The specific objective of this study was to investigate the use of red mud based on the “simulation” integrating the sustainability aspect through the PROMETHEE method. The data source is from a field survey with experts conducted at the research location from the province of West Kalimantan, Indonesia. The results of the study using the PROMETHEE ranking parameter showed that the best optimal industrial cluster sites were Ketapang, followed by Belitung Island, Mempawah, and Teluk Batang, with scores of 0.4167, 0.0476, 0.0, and −0.463, respectively. However, using economic input and environmental output, the efficient frontier showed that Ketapang, Teluk Batang, and Pulau Belitung are efficient sites. Considerably more work will need to be carried out to determine the strategic partner in the increasing significant added value in the red mud industrial cluster sites.

MgB₂/CNT is a promising candidate for superconducting wire application due to its excellent mechanical properties and carbon nanotube’s low density. However, strong interfacial adhesion between the CNT reinforcement and the MgB₂ matrix is difficult to manage. Therefore, this study examines the synthesis and characterization of magnesium diboride (MgB₂) superconductors with carbon nanotubes (CNTs) and tin (Sn) addition. Determining the proper method and combination of CNT & Sn affects MgB₂ superconductors is crucial. Raw materials of magnesium (Mg), boron (B), Sn, and multi-walled carbon nanotubes (MWCNTs) were used for a solid-state reaction process to determine the proper synthesis method and the effect of CNT on superconductors’ critical temperature. Each sample was obtained by weighing the raw material first, followed by hand grinding with agate mortars for 3 hours. The pelletization was then conducted by using a compact pressing machine with a pressure of 350 MPa. The compacted samples were then sintered at 800 °C for 2 hours either through the vacuum or PIST process. Finally, all were characterized, and MgB₂ was discovered to be the dominant phase with minor impurity phases such as MgO, Mg, Mg₂Sn, C, and Sn. Based on SEM morphological analysis, the grain boundaries of sample A1 were more precise than B2. In both, the grain size also varies, and the distribution of elements is uneven. Subsequently, Cryogenic Magnet Characterization indicated that at 40 K, almost all samples possess superconducting characteristics. For future studies, the potential impact of MgB₂ on critical current density (Jc) and magnetic density (Hc) in several commercial applications such as Magnetic Resonance Imaging (MRI), magnetic levitation, and transformers needs to be investigated