We demonstrate the design and fabrication of novel Cu ₂ O@Mn(OH) ₂ core–shell hierarchical structures using octahedral Cu ₂ O as a template.

Toluene is extensively used in many industrial products, which needs to be effectively detected by sensitive gas sensors even at low-ppm-level concentrations. Here, NiFe₂O₄ nano-octahedrons were calcinated from NiFe-bimetallic metal-organic framework (MOFs) octahedrons synthesized by a facile refluxing method. The co-existence of p-Phthalic acid (PTA) and 3,3-diaminobenzidine (DAB) promotes the formation of smooth NiFe-bimetallic MOFs octahedrons. After subsequent thermal treatment, a big weight loss (about 85%) transformed NiFe₂O₄ nanoparticles (30 nm) into NiFe₂O₄ porous nano-octahedrons with hollow interiors. The NiFe₂O₄ nano-octahedron based sensor exhibited excellent gas sensing properties for toluene with a nice stability, fast response, and recovery time (25 s/40 s to 100 ppm toluene), and a lower detection limitation (1 ppm) at 260 °C. The excellent toluene-sensing properties can not only be derived from the hollow interiors combined with porous nano-octahedrons to favor the diffusion of gas molecules, but also from the efficient catalytic activity of NiFe₂O₄ nanoparticles.

The moderation of the dielectric properties of polymer composites and their environmental stability need to be considered comprehensively in the design of microwave-absorbing materials. In this work, polypyrrole/polystyrene (PPy/PS) composited particles were synthesized through a facile in situ bulk polymerization procedure. The PS component can be modulated conveniently by controlling the polymerization time. FTIR and Raman analyses disclosed that the PS component was immobilized in PPy via covalent bonds. The electromagnetic characterization results indicated that the dielectric properties and, thus, the microwave absorption could be controlled when the styrene polymerization was prolonged from 6 h (PPy-6) to 19 h (PPy-19). The composite PPy-19 displayed an optimal reflection loss of −51.7 dB with a matching thickness of 3.16 mm, and the effective absorption bandwidth (EAB) even reached 5.8 GHz at 2.4 mm. The PS component endowed PPy/PS composites with more robust environmental stability than homogeneous PPy. After being exposed to air for 365 days and hydrothermally treated at 100 °C for 12 h, PPy-19 still exhibited a reflection loss superior to −20 dB. The present work provides a new insight into the adjustment of the electromagnetic properties of PPy composites to fabricate high-performance microwave absorbers with superior environmental stability.

As a typical spinel ferrite, NiFe₂O₄ is suitable for use in gas sensors. Herein, we report the fabrication of porous, tremella-like NiFe₂O₄ assembled using porous, ultrathin nanosheets via the coordination of Ni²⁺ and Fe²⁺ with 1,4-phenylenediboronic acid. The optical band gap of the NiFe₂O₄ is estimated to be about 1.7 eV. Furthermore, the NiFe₂O₄ sensor annealed at 400 °C exhibits a low detection limit of 50 ppb, a fast response/recovery time (11.6 s/41.9 s to 10 ppm toluene), good reproducibility, and long-term stability at 220 °C. The suitable sensing performances can be attributed to the good catalytic activity of NiFe₂O₄ to toluene oxidation. Moreover, the ultrathin nanosheets with porous structures provide a large number of active sites to significantly favor the diffusion and adsorption/desorption of toluene molecules. This current work provides an insight into fabricating NiFe₂O₄ using 1,4-phenylenediboronic acid, which is promising for ppb-level toluene detection.

Ni-MOF, as a metal–organic framework, has the advantages of morphological diversity and adjustable composition, which make its derivatives attractive for electromagnetic wave absorption. However, it is challenging for Ni-MOF derivatives to obtain strong absorption at low filling rates. Herein, ternary Ni@C/PPy composites based on Ni-MOF derivatives were synthesized by cooperatively coupling magnetic Ni@C nanoparticles with a conductive polymer PPy matrix through a facile self-assembly method. Among them, Ni@C nanoparticles are formed after Ni-MOF pyrolysis, and PPy serves as the backbone to effectively assemble and support the Ni@C nanoparticles. As a result, the Ni@C/PPy-3 sample exhibited excellent performance with a reflection loss value of −50.65 dB at a filling ratio of 15 wt% and a thickness of 2.5 mm. At the same time, its effective absorption bandwidth reached 6.24 GHz, covering the whole Ku frequency band. The results show that in comparison to pure Ni@C composite, the Ni@C/PPy multi-component composite with a porous structure shows significant advantages in terms of optimizing impedance matching, which can effectively enhance the interface polarization and, thus, greatly improve its electromagnetic absorption ability. In summary, this work provides a valuable research idea for developing strong absorbing properties of absorbing materials at a low filling rate.