With the continuous industrialization, as one of the most common air pollutants found in fossil fuels and automobile exhausts, nitride oxide (NO ₂ ) monitor is very essential for ensuring good air quality and our body health. 2D materials attract more attention for its special surface and electron structures. MoS ₂ shows small gas sensing response for its less surface dangling bonds. Here, we introduce a facile method to modify MoS ₂ with SnO ₂ as a NO ₂ receptor via mechanical composite. The MoS ₂ nanoflowers prepared with a hydrothermal method depicted a high surface/volume ratio and the SnO ₂ fabricated using a solvothermal method. Mixing ratio and annealing temperature was systematic researched for screening optimal parameters for gas sensor fabrication. The response was enhanced 1.5 time after modification with fast response and recovery time. The p-n heterostructure also provide good selectivity towards NO ₂ for gas sensing. This work provides a facile alternative for fast and stable response NO ₂ gas sensor at room temperature.

A highly sensitive and precise Love wave mode surface acoustic wave (SAW) immunosensor based on an ST-cut 90°X quartz substrate and an SiO₂ wave-guiding layer was developed to detect cancer-related biomarkers of carcinoembryonic antigens (CEAs). A delay line structure of the SAW device with a resonant frequency of 196 MHz was designed/fabricated, and its surface was functionalized through CEA antibody immobilization. The CEA antibodies were bound with gold nanoparticles and CEA antibodies to form a sandwich structure, which significantly amplified the mass loading effect and enhanced the maximum responses by 30 times. The center frequency of the Love wave immunosensor showed a linear response as a function of the CEA concentration in the range of 0.2–5 ng/mL. It showed a limit of detection of 0.2 ng/mL, and its coefficient of determination was 0.983. The sensor also showed minimal interference from nonspecific adsorptions, thus demonstrating its promise for point-of-care applications for cancer biomarkers.

Ammonia (NH₃) gas is prevalent in industrial production as a health hazardous gas. Consequently, it is essential to develop a straightforward, reliable, and stable NH₃ sensor capable of operating at room temperature. This paper presents an innovative approach to modifying SnO₂ colloidal quantum dots (CQDs) on the surface of Ti₃C₂T_x MXene to form a heterojunction, which introduces a significant number of adsorption sites and enhances the response of the sensor. Zero-dimensional (0D) SnO₂ quantum dots and two-dimensional (2D) Ti₃C₂T_x MXene were prepared by solvothermal and in situ etching methods, respectively. The impact of the mass ratio between two materials on the performance was assessed. The sensor based on 12 wt% Ti₃C₂T_x MXene/SnO₂ composites demonstrates excellent performance in terms of sensitivity and response/recovery speed. Upon exposure to 50 ppm NH₃, the frequency shift in the sensor is −1140 Hz, which is 5.6 times larger than that of pure Ti₃C₂T_x MXene and 2.8 times higher than that of SnO₂ CQDs. The response/recovery time of the sensor for 10 ppm NH₃ was 36/54 s, respectively. The sensor exhibited a theoretical detection limit of 73 ppb and good repeatability. Furthermore, a stable sensing performance can be maintained after 30 days. The enhanced sensor performance can be attributed to the abundant active sites provided by the accumulation/depletion layer in the Ti₃C₂T_x/SnO₂ heterojunction, which facilitates the adsorption of oxygen molecules. This work promotes the gas sensing application of MXenes and provides a way to improve gas sensing performance.

Nitrogen dioxide is one origin of air pollution from fossil fuels with the potential to cause great harm to human health in low concentrations. Therefore, low-cost, low-power-consumption sensors for low-concentration NO₂ detection are essential. Herein, heterojunction by SnO₂ quantum wires, a traditional metal oxide NO₂ sensing material, and Ti₃C₂T_x MXene, a novel type of 2D layered material, was synthesized using a simple solvothermal method for enhancing gas-sensing performance and reducing operating temperature. The operating temperature was reduced to 80 °C, with a best performance of 27.8 and a fast response and recovery time (11 s and 23 s, respectively). The SnO₂ and Ti₃C₂T_x MXene composite exhibits high speed and low detection limit due to the construction of the heterojunction with high conductive Ti₃C₂T_x MXene. The selectivity and stability of gas sensors are carried out. This could enable the realization of fast response, high-sensitivity, and selective NO₂ sensing under low operating temperatures.