A donor–acceptor (D–A) cruciform conjugated luminophore DMCS-TPA was designed and synthesized. The DMCS-TPA solid shows both aggregation induced emission (AIE) effect and high contrast mechanochromic (MC) behavior with a remarkable spectral shift of 87 nm. The obvious fluorescence switching from yellowish green to orange can be realized by pressing at only 10 MPa or simply grinding. The photophysical properties, theory calculation and XPS results demonstrate that the extension of the conjugation length and subsequent enhancement of intramolecular charge transfer (ICT) transition are responsible for the improved MC performance. In addition, DMCS-TPA is readily deposited on the ITO electrode surface by the electrochemical method to form an electrochromic (EC) film with multiple colours showing (light green at 0 V, red at 1 V, grey at 1.1 V and blue at 1.45 V) and a high optical contrast of 65% at 769 nm. The results suggest that incorporation of electroactive moieties into luminophores to constitute D–A cruciform conjugated structures is a promising design strategy for preparing dual functional materials combining MC and EC properties.

Cyanostilbene derivatives with the aggregation-induced emission enhancement (AIEE) activity are prepared by Knoevenagel and Suzuki reactions. Among them, the dye (Z)-2,3-bis(4′-(diphenylamino)-[1,1′-biphenyl]-4-yl)acrylonitrile (CNS-4) nanoparticle suspension shows the polarity-dependent characteristics of the fluorescence properties. By the fluorescence spectroscopy and transmission electron microscopy (TEM) analysis, the restriction of transfer from the local excited (LE) state to the intramolecular charge-transfer (ICT) state and crystal formation results in a blue-shift in emission and enhances the intensity in the aggregate state. Additionally, the luminophors CNS-3 and CNS-4 possess the AIEE effect as well as mechanochromic fluorescent properties. This mechanofluorochromic behavior originates from the change between the crystalline and the amorphous state.

Cruciform D-A π-architecture is proposed as a platform for constructing bifunctional optoelectronic materials, in which the ICT from donor axis to acceptor axis can be finely tuned to regulate mechanochromic and electrochromic properties.

Catheter-associated urinary tract infections are one of the most common hospital-acquired infections. Encrustation formation results from infection of urease-producing bacteria and further complicates the situation. A typical sign of the initial onset of encrustation formation is the alkalization of the urine (pH up to 9–10). However, effective antibacterial strategies with high antimicrobial loading efficiency and pH-responsiveness of antimicrobial release are still lacking. In this study, we developed a poly(sulfobetaine methacrylate)-tannic acid (polySBMA-TA) hydrogel coating, which served as a universal, efficient, and responsive carrier for antimicrobials on urinary catheters. Common antimicrobials, including poly(vinylpyrrolidone)-iodine, copper ions, and nitrofurazone were loaded into the polySBMA-TA coating in high efficiency (several fold higher than that of the polySBMA coating), via the formation of multiple non-covalent interactions between the antimicrobials and hydrogel coating. The hydrogel coatings maintained good antibacterial properties under neutral conditions. More importantly, the pH-responsive release of antibacterial agents under alkaline conditions further enhanced the antibacterial activity of the coatings, which was advantageous for killing the urease-producing bacteria and preventing encrustation. In vitro and in vivo tests confirmed that the hydrogel coating has good biocompatibility, and could effectively inhibit bacterial colonization and encrustation formation. This study offers new opportunities for the utilization of a simple and universal antimicrobial-loaded hydrogel coating with smart pH-responsive properties to combat bacterial colonization and encrustation formation in urinary catheters.

A star-shaped thiophene derivative, namely PHBT, consisting of one central core of phenyl and three arms of bithiophene, was newly synthesized and characterized, in order to further investigate the relationship between the star-shaped monomer structure (central core and peripheral arm) and the polymeric electrochromic properties. Then it was further successfully prepared into the corresponding cross-linked polymer pPHBT via electrochemical polymerization. After applying positive voltage, pPHBT exhibited excellent electrochromic properties with surprising multi-color changes between three colors, orange-yellow, green and blue, and a fast color switching speed. Furthermore, electronic structure, cyclic voltammetry and electrochromic results of pPHBT can contribute much to explain the electrochromic behavior of pTPABT with the triphenylamine core and the quadruple thiophene arm. The electrochromism of pTPABT might consist of two parts derived from the oxidative states of triphenylamine and quadruple thiophene groups, respectively. This offers a new insight into the electrochromism mechanics of conjugated polymers.