Our earlier research indicated that chitosan-gentamicin conjugate (CS-GT) possesses superior antimicrobial activity and good water solubility. To develop CS-GT-based scald dressings, the antibacterial properties of CS-GT were further studied, and the biosafety of CS-GT and the healing mechanism of CS-GT hydrogel was systematically explored in this article. It was found that cell viability shows a declined inclination with the prolonged culture time and the increased concentration of CS-GT. After three day’s culture, the cell viability could still remain at 79.72% when CS-GT concentration was as high as 1000 μg/mL. On the other hand, the hemolysis rate of CS-GT was lower than 5% when its concentration is 800 μg/mL. Therefore CS-GT has good cytocompatibility and hemocompatibility. A wound-healing experiment has shown that the skin healing rate of CS-GT hydrogel was the highest at 99.61%, followed by the positive control (wet burn ointment) 94.98%, GT hydrogel 87.50%, and matrix 77.39%. The blank control group, however, possessed the lowest healing rate of 75.45%. Further analysis indicated that CS-GT hydrogel could promote the synthesis of total protein (TP) in skin granulation tissue, resulting in the enhanced hydroxyproline (HYP) content, which facilitated collagen fibrogenesis, reduced cytokine expression in an inflammatory response, and, ultimately, accelerated wound healing. To sum up, CS-GT hydrogel is a promising scald dressing.

When the aquaculture water environment deteriorates or the temperature rises, shrimp are susceptible to viral or bacterial infections, causing a large number of deaths. This study comprehensively evaluated the effects of the oral administration of a chitosan–gentamicin conjugate (CS-GT) after Litopenaeus vannamei were infected with Vibrio parahaemolyticus, through nonspecific immunity parameter detection, intestinal morphology observation, and the assessment of microbial flora diversification by 16S rRNA gene sequencing. The results showed that the oral administration of CS-GT significantly increased total hemocyte counts and reduced hemocyte apoptosis in shrimp (p < 0.05). The parameters (including superoxide dismutase, glutathione peroxidase, glutathione, lysozyme, acid phosphatase, alkaline phosphatase, and phenoloxidase) were significantly increased (p < 0.05). The integrity of the intestinal epithelial cells and basement membrane were enhanced, which correspondingly alleviated intestinal injury. In terms of the microbiome, the abundances of Vibrio (Gram-negative bacteria and food-borne pathogens) in the water and gut were significantly reduced. The canonical correspondence analysis (CCA) showed that the abundances of Vibrio both in the water and gut were negatively correlated with CS-GT dosage. In conclusion, the oral administration of CS-GT can improve the immunity of shrimp against pathogenic bacteria and significantly reduce the relative abundances of Vibrio in aquaculture water and the gut of Litopenaeus vannamei.

To develop a novel asymmetric nanofiber membrane with antioxidant and antibacterial activities, biocompatible polyvinyl pyrrolidone (PVP) and polycaprolactone (PCL) were used as carriers to load water-soluble tea tree extract (TTE) and hydrophobic tea tree oil (TTO) via electrospinning and electrostatic spraying, respectively, which was named as TTE-PVP-3/TTO-PCL. The results show that uniform TTE-PVP nanofibers with an average diameter of 95 ± 27 nm could be obtained when the mass ratio of TTE to PVP was set as 1:3. Homogeneous TTO/PCL microspheres with an average size of 4.38 ± 0.79 µm could be obtained when the propulsion speed was 0.08 mm/min and the voltage was 10 KV. The activity study showed that TTE could only improve the antioxidant activity of TTE-PVP-3/TTO-PCL, while TTO could improve the antibacterial activity effectively. Under experimental conditions, the inhibition zones of TTE-PVP-3/TTO-PCL against Staphylococcus aureus and Escherichia coli were 7.50 ± 0.48 mm and 9.55 ± 0.45 mm, respectively, and its scavenging rates for 2,2-diphenylpicrylhydrazyl (DHPP) and hydroxyl radical were 59.79 ± 4.10% and 61.02 ± 4.95%, respectively. In conclusions, TTE-PVP-3/TTO PCL can be potentially used as a new kind of anti-oxidative and antibacterial wound dressings.

Functional carbon materials have been developed and applied in various sewage treatment applications in recent years. This article reports the fabrication, characterization, and application of a new kind of poly (allylthiourea-co-acrylic acid) (PAT–PAC) hydrogel-based carbon monolith. The results indicated that the poly acrylic acid component can endow the PAT–PAC hydrogel with an increased swelling ratio and enhanced thermal stability. During the carbonization process, O–H, N–H, C=N, and –COO– groups, etc. were found to be partly decomposed, leading to the conjugated C=C double bonds produced and the clear red shift of C=O bonds. Particularly, it was found that this shift was accelerated under higher carbonization temperature, which ultimately resulted in the complex conjugated C=C network with oxygen, nitrogen, and sulfur atoms doped in-situ. The as-obtained carbon monoliths showed good removal capacity for Ni(II) ions, organic solvents, and dyes, respectively. Further analysis indicated that the Ni(II) ion adsorption process could be well described by pseudo-second-order and Freundlich models under our experimental conditions, respectively. The adsorption capacity for Ni(II) ions and paraffin oil was as high as 557 mg/g and 1.75 g/g, respectively. More importantly, the as-obtained carbon monoliths can be recycled and reused for Ni(II) ions, acetone, and paraffin oil removal. In conclusion, the proposed PAT–PAC-based carbonaceous monoliths are superior adsorbents for wastewater treatment.