In the present paper, we address the influence of print orientation angle on surface roughness obtained in lateral walls in fused deposition modelling (FDM) processes. A geometrical model is defined that considers the shape of the filaments after deposition, in order to define a theoretical roughness profile, for a certain print orientation angle. Different angles were considered between 5° and 85°. Simulated arithmetical mean height of the roughness profile, Ra values, were calculated from the simulated profiles. The Ra simulated results were compared to the experimental results, which were carried out with cylindrical PLA (polylactic acid) samples. The simulated Ra values were similar to the experimental values, except for high angles above 80°, where experimental roughness decreased while simulated roughness was still high. Low print orientation angles show regular profiles with rounded peaks and sharp values. At a print orientation angle of 85°, the shape of the profile changes with respect to lower angles, showing a gap between adjacent peaks. At 90°, both simulated and experimental roughness values would be close to zero, because the measurement direction is parallel to the layer orientation. Other roughness parameters were also measured: maximum height of profile, Rz, kurtosis, Rku, skewness, Rsk, and mean width of the profile elements, Rsm. At high print orientation angles, Rz decreases, Rku shifts to positive, Rsk slightly increases, and Rsk decreases, showing the change in the shape of the roughness profiles.

Prostheses made from ceramic materials have the advantages of producing little debris and having good durability, compared with those made from metal and plastic. For example, hip prostheses require a porous external area that allows their fixation by means of osseointegration and a solid internal area that will be in contact with the femoral head. The manufacturing of complex ceramic shapes, by means of machining processes, for example, is complicated and can lead to breakage of the parts because of their fragility. The direct ink writing (DIW) process allows the printing of ceramic pastes into complex shapes that achieve their final strength after a heat treatment operation. This paper studies both the dimensional error and surface finish of porous zirconia prismatic parts prior to sintering. The variables considered are infill, layer height, printing speed, extrusion multiplier and bed temperature. The responses are the dimensional error of the lateral walls of the samples and an areal roughness parameter, the arithmetical mean height, Sa. Mathematical models are found for each response, and multiobjective optimization is carried out by means of the desirability function. The dimensional error depends mainly on the interaction between layer height and infill, while the roughness on the interaction between infill and printing speed. Thus, infill is an important factor for both responses. In the future, the behavior of compact printed parts will be addressed.

Three-dimensional printing is revolutionizing the development of scaffolds due to their rapid-prototyping characteristics. One of the most used techniques is fused filament fabrication (FFF), which is fast and compatible with a wide range of polymers, such as PolyLactic Acid (PLA). Mechanical properties of the 3D printed polymeric scaffolds are often weak for certain applications. A potential solution is the development of composite materials. In the present work, metal-PLA composites have been tested as a material for 3D printing scaffolds. Three different materials were tested: copper-filled PLA, bronze-filled PLA, and steel-filled PLA. Disk-shaped samples were printed with linear infill patterns and line spacing of 0.6, 0.7, and 0.8 mm, respectively. The porosity of the samples was measured from cross-sectional images. Biocompatibility was assessed by culturing Human Bone Marrow-Derived Mesenchymal Stromal on the surface of the printed scaffolds. The results showed that, for identical line spacing value, the highest porosity corresponded to bronze-filled material and the lowest one to steel-filled material. Steel-filled PLA polymers showed good cytocompatibility without the need to coat the material with biomolecules. Moreover, human bone marrow-derived mesenchymal stromal cells differentiated towards osteoblasts when cultured on top of the developed scaffolds. Therefore, it can be concluded that steel-filled PLA bioprinted parts are valid scaffolds for bone tissue engineering.

At present, laser cutting is currently employed to cut metallic plates, due to their good finish and dimensional quality, as well as because of the flexibility of the process to obtain different shapes. In the present paper, surface roughness, dimensional accuracy, and burr thickness of thin plates of 0.8 mm are studied as functions of different process parameters: pulse frequency, pulse width, and speed. Eight different experiments were performed according to a full 2³ factorial design, with two replicates each. Square specimens of 10 mm × 10 mm were cut. Arithmetical mean roughness Ra was measured with a contact roughness meter, and the dimensions and burr thickness with a micrometer. Ra values ranged between 1.89 and 3.86 µm, dimensional error values between 0.22 and 0.93%, and burr thickness between 2 and 34 µm. Regression analysis was performed, and linear models were obtained for each response. Results showed that roughness depends mainly on frequency, on the interaction of frequency and pulse width and on pulse width. Dimensional error depends on pulse width, frequency, and the interaction between pulse width and speed. Burr thickness is influenced by frequency, pulse width, and the interaction between frequency and speed. Multi-objective optimization showed that, in order to simultaneously minimize the three responses, it is recommended to use high frequency (80 Hz), high pulse width (0.6 ms), and high speed (140 mm/min). The present study will help to select appropriate laser cutting conditions in thin plates, in order to favor good surface finish and dimensional accuracy, as well as low burr thickness.

Honing processes provide a special cross-hatch pattern to the internal surface of cylinders that favors oil flow. However, along honing operation the abrasive grains wear out and lose their ability to cut material. The honing chips mixed with oil fill the pores of the abrasives and they start cutting in an incorrect way, leading to clogging. In the present paper, honing experiments were carried out according to a 3² factorial design, with different grain size and density of abrasive grains. Roughness, material removal rate, and tool wear were determined. Acoustic emissions were also measured and the chirplet concept was applied in order to detect differences between correct and incorrect cutting operations. As a general trend roughness and material removal rate increase with grain size and with density of abrasive. However, when clogging occurs roughness and material removal rate decrease, because the abrasive grains tend to deform the material instead of cutting it. When the honing process is working appropriately, the chirplet diagram of the harmonic part of the signal shows constant marks. On the contrary, when it does not work properly, marks disappear with time and their frequencies decrease. The results of the present paper will allow monitoring the honing process in order to change the abrasives when they are not working properly.

The purpose of this study is to characterize two different 3D-printed materials, glass fiber-filled polypropylene (GF-PP) and calcium carbonate-filled polypropylene (CaCO₃-PP), which make it possible to obtain surgical bone models at a reasonable cost. The methodology involved selecting two filaments, among six, which showed better processability in the fused filament fabrication (FFF) process. Then, samples of the two selected materials were 3D printed, followed by characterization in terms of dimensional error, porosity, surface roughness, and mechanical strength. The results showed that both materials can be sterilized, with an increase in dimensional error and porosity after sterilization and slight changes in roughness and tensile strength. Additionally, anatomical models of mandible and femur bones were clinically validated by surgeons.