k-Oligocarrageenan (OC) is an effective biostimulator and a protector against disease infections for plants. However, the effect of OC molecular weight (MW) on plant growth is not fully understood. In this work, OCs with three different MWs (42, 17 and 4 kDa) was prepared by varying the degradation reaction time using ascorbic acid as a reagent. The product structure was confirmed by Fourier-transform infrared spectroscopy (FTIR) data. The growth promotion for maize (Zea mays L.) plants was investigated by foliar spray application of the prepared OCs. Field trials were carried out in two years, 2018 and 2019. The results showed that among treatments, OC with 4 kDa exhibited the best performance in both crop growth and grain yield parameters which indicated increases compared to the control in plant height (6.9–19.9%), length of ears (12.2%), diameter of ears (9.1%), fresh grain weight (17.8%), dry grain weight (20.0%) and grain yield (21.3%). Moreover, low MW OC augmented NP uptake in the plant growth while no effect on K uptake was observed. Therefore, OC with low MWs is potentially promising to apply as a promoter to enhance yield of crops.

Spherical zinc is well known as an effective pigment for the corrosion protection of carbon steel. However, a high proportion of spherical Zn in a coating leads to difficulties in fabricating the coating solution and increased cost. In this work, the influence of flake ZnAl alloy in silicate coatings on the corrosion protection properties of steel substrates was investigated. The electrochemical behaviour of coatings containing different flake ZnAl alloy content immersed in NaCl solution (3.5 wt%) was evaluated using an electrochemical impedance spectroscopy (EIS) method. A salt spray test was performed to evaluate corrosion on the coating surface. Pull-off tests of the coatings before and after the salt spray process were performed, and the surface morphology was analysed to determine the degradation of corrosion resistance. The results show that silicate coating containing flake ZnAl alloy (25 wt%) possesses the highest total resistance (1417 Ω) and the longest time to the appearance of white rust (720 h). The surface morphology of the coating containing 25 wt% flake ZnAl alloy was found to include corrosion products with the most compacted surface, which effectively prevents the penetration of electrolytes to the interface between the coating and the steel.