Rotation during reaction: Determining changes in heterogeneous catalysts under reaction conditions can provide insight into mechanisms. Under reaction conditions, not only can metal nanoparticles change shape but their interaction with the oxide support could also be affected. Yuan et al. used aberration-corrected environmental transmission electron microscopy to study gold nanoparticles on titanium surfaces at low electron beam doses. During carbon monoxide (CO) oxidation at total pressures of a few millibars and 500°C, they observed that gold nanoparticles rotated by about 10° but returned to their original position when CO was removed. Density function theory calculations indicated that rotation was induced by changes in the coverage of adsorbed molecular oxygen at the interface. Science , this issue p. 517

Imaging reactive surface water: Recent developments in transmission electron microscopy (TEM) have enabled imaging of single atoms, but adsorbed gas molecules have proven more challenging because of a lack of sufficient image contrast. Yuan et al. adsorbed water and carbon monoxide (CO) on a reconstructed nanocrystalline anatase titanium dioxide (TiO ₂ ) surface that has protruding TiO ₃ ridges every four unit cells, which provide regions of distinct contrast. Water adsorption on this surface during environmental TEM experiments led to the formation of twinned protrusions. These structures developed dynamic contrast as the water reacted with coexposed CO to form hydrogen and carbon dioxide. Science , this issue p. 428

A grand unified model (GUM) is developed to achieve fundamental understanding of rich structures of all 71 liganded gold clusters reported to date. Inspired by the quark model by which composite particles (for example, protons and neutrons) are formed by combining three quarks (or flavours), here gold atoms are assigned three ‘flavours’ (namely, bottom, middle and top) to represent three possible valence states. The ‘composite particles’ in GUM are categorized into two groups: variants of triangular elementary block Au₃(2e) and tetrahedral elementary block Au₄(2e), all satisfying the duet rule (2e) of the valence shell, akin to the octet rule in general chemistry. The elementary blocks, when packed together, form the cores of liganded gold clusters. With the GUM, structures of 71 liganded gold clusters and their growth mechanism can be deciphered altogether. Although GUM is a predictive heuristic and may not be necessarily reflective of the actual electronic structure, several highly stable liganded gold clusters are predicted, thereby offering GUM-guided synthesis of liganded gold clusters by design.