Biochar has shown great promise in producing low-cost low-carbon concrete for civil infrastructure applications. However, there is limited research comparing the use of pristine and contaminated biochar in concrete. This paper presents comprehensive laboratory experiments and three-dimensional nonlinear finite element analysis on the mechanical, economical, and environmental performance of reinforced concrete beams made using concrete blended with biochar generated from vetiver grass roots after the roots were used in an oil extraction process. Both pristine biochar and biochar that were used to treat wastewater through adsorbing heavy metals (100 mg/L of Pb, Cu, Cd, and Zn) were investigated. The biochar was used to replace up to 6% Portland cement in concrete. Laboratory experiments were conducted to characterize the workability, mechanical properties, shrinkage, and leaching potential of the concrete blended with biochar. The results showed that using biochar could increase the compressive strengths and reduce the shrinkage of concrete without causing a leaching problem. The results from finite element analysis of the reinforced concrete beams showed that the use of biochar was able to increase the flexural performance of the beams as well as their economic and environmental performance. This research will promote the development and structural applications of low-cost low-carbon concrete.

Vetiver grass (Chrysopogon zizanioides) is well-known for its contaminant phytoextraction potential and its capacity to reduce soil erosion, owing to its massive, dense root system. However, the shoots are not major contributors to either of these processes, and are either not utilized at all or they become part of the waste stream. It is well-recognized that lignocellulosic biomass can serve as a source of raw material to produce second-generation bioethanol. This study investigated the simultaneous saccharification and fermentation (SSF) of acid–alkali pretreated vetiver (VG) shoots by Saccharomyces cerevisiae. Vetiver shoots were obtained from three sources: (1) shoots from VG grown in clean potting soil, (2) shoots from VG used for antibiotics phytoextraction from a constructed wetland setup, and (3) shoots from VG used for lead phytoextraction during soil remediation. Bioethanol yield from the shoots from clean soil was the highest (19.58 g/L), followed by the one used for lead phytoextraction (19.50 g/L) and the one used for antibiotics phytoextraction (19.17 g/L). Bioethanol yield and quality obtained from these three VG shoots was superior or similar to other C4 grasses used for bioethanol generation. This study successfully demonstrated that spent vetiver biomass after phytoextraction applications can be repurposed to generate high-quality bioethanol.

Vetiver root is widely used to produce essential oils in the aromatherapy industry. After the extraction of oil, the roots are disposed of as waste. The central objective of this research was to explore the conversion of this waste into a resource using a circular economy framework. To generate biochar, vetiver roots were pyrolyzed at different temperatures (300, 500, and 700 °C) and residence times (30, 60, and 120 min). Analysis showed the root biochar generated at 500 °C and held for 60 min had the highest surface area of 308.15 m²/g and a yield of 53.76%, in addition to other favorable characteristics. Comparatively, the surface area and the yield of shoot biochar were significantly lower compared to those of the roots. Repurposing the spent root biomass for environmental and agronomic benefits, our circular economy concept prevents the plant tissue from entering landfills or the waste stream.