The molecular functionalization of two-dimensional MoS₂ is of practical relevance with a view to, for example, facilitating its liquid-phase processing or enhancing its performance in target applications. While derivatization of metallic 1T-phase MoS₂ nanosheets has been relatively well studied, progress involving their thermodynamically stable, 2H-phase counterpart has been more limited due to the lower chemical reactivity of the latter. Here, we report a simple electrolytic strategy to functionalize 2H-phase MoS₂ nanosheets with molecular groups derived from organoiodides. Upon cathodic treatment of a pre-expanded MoS₂ crystal in an electrolyte containing the organoiodide, water-dispersible nanosheets derivatized with acetic acid or aniline moieties (∼0.10 molecular groups inserted per surface sulfur atom) were obtained. Analysis of the functionalization process indicated it to be enabled by the external supply of electrons from the cathodic potential, although they could also be sourced from a proper reducing agent, as well as by the presence of intrinsic defects in the 2H-phase MoS₂ lattice (e.g., sulfur vacancies), where the molecular groups can bind. The acetic acid-functionalized nanosheets were tested as a non-noble metal-based catalyst for nitroarene and organic dye reduction, which is of practical utility in environmental remediation and chemical synthesis, and exhibited a markedly enhanced activity, surpassing that of other (1T- or 2H-phase) MoS₂ materials and most non-noble metal catalysts previously reported for this application. The reduction kinetics (reaction order) was seen to correlate with the net electric charge of the nitroarene/dye molecules, which was ascribed to the distinct abilities of the latter to diffuse to the catalyst surface. The functionalized MoS₂ catalyst also worked efficiently at realistic (i.e., high) reactant concentrations, as well as with binary and ternary mixtures of the reactants, and could be immobilized on a polymeric scaffold to expedite its manipulation and reuse.

Phosphate-functionalized carbon-based nanomaterials have attracted significant attention in recent years owing to their outstanding behavior in electrochemical energy-storage devices. In this work, we report a simple approach to obtain phosphate-functionalized graphene (PFG) via anodic exfoliation of graphite at room temperature with a high yield. The graphene nanosheets were obtained via anodic exfoliation of graphite foil using aqueous solutions of H₃PO₄ or Na₃PO₄ in the dual role of phosphate sources and electrolytes, and the underlying exfoliation/functionalization mechanisms are proposed. The effect of electrolyte concentration was studied, as low concentrations do not lead to a favorable graphite exfoliation and high concentrations produce fast graphite expansion but poor layer-by-layer delamination. The optimal concentrations are 0.25 M H₃PO₄ and 0.05 M Na₃PO₄, which also exhibited the highest phosphorus contents of 2.2 and 1.4 at. %, respectively. Furthermore, when PFG-acid at 0.25 M and PFG-salt at 0.05 M were tested as an electrode material for capacitive energy storage in a three-electrode cell, they achieved a competitive performance of ∼375 F/g (540 F/cm³) and 356 F/g (500 F/cm³), respectively. Finally, devices made up of symmetric electrode cells obtained using PFG-acid at 0.25 M possess energy and power densities up to 17.6 Wh·kg^–1 (25.3 Wh·L^–1) and 10,200 W/kg; meanwhile, PFG-salt at 0.05 M achieved values of 14.9 Wh·kg^–1 (21.3 Wh·L^–1) and 9400 W/kg, with 98 and 99% of capacitance retention after 10,000 cycles, respectively. The methodology proposed here also promotes a circular-synthesis process to successfully achieve a more sustainable and greener energy-storage device.