Purpose: A major challenge in ocular therapeutics is poor bioavailability of drug, 1% or even less of the instilled dose is absorbed and frequent administration of conventional products leads to poor adherence to therapy. Hence the present study is to synthesize N-trimethyl chitosan (TMC), a water-soluble chitosan derivative and to prepare flurbiprofen (FLU):hydroxyl propyl-β-cyclodextrin (HP-β-CD) complex loaded nanoparticles for treatment of bacterial conjunctivitis which aims to increase the residence time in ocular tissue thus enhancing patient compliance and improved efficacy. Methods: TMC was synthesized and characterized by ¹H NMR and FT-IR. TMC and chitosan (CS) nanoparticles containing inclusion complex were prepared by ionic gelation using sodium tripolyphosphate (TPP). The nanoparticles thus obtained were evaluated for particle size, zeta potential, drug entrapment, in-vitro release, in-vitro mucoadhesion and TEM for morphology and irritation potential was evaluated by the HET-CAM technique. Results: N-methyl quaternization of CS was confirmed by ¹H NMR. The particle size and zeta potential of the TMC nanoparticles were found to be 201 ± 1.55 nm and +13.9 ± 1.697 mV and that of CS nanoparticles were 361.2 ± 1.55 nm and +10.9 ± 0.424 mV respectively. The entrapment of FLU- HP-β-CD inclusion complex in polymeric nanoparticles was found to be 10.91 ± 1.541%. The observed in-vitro release profile of TMC nanoparticles indicated characteristic burst release followed by delayed release. HET-CAM studies demonstrated the ocular safety of TMC nanoparticles. Conclusion: The developed TMC nanoparticles offered prolonged release potential for transmucosal ocular delivery of hydrophobic flurbiprofen.

Chitosan (CS) is a biodegradable, biocompatible, and mucoadhesive natural polymer soluble in acidic pH only and can be irritating to the eye. Objective of the study was to synthesize water soluble 6-O-carboxymethyl (OCM-CS) derivative of CS, and to develop CS and OCM-CS nanoparticles (NPs) loaded with dorzolamide hydrochloride (DRZ). CS was reacted with monochloroacetic acid (MCA) for OCM-CS synthesis and was characterized by FT-IR, DSC, and ¹³C NMR. CS and OCM-CS NPs were prepared by ionic gelation method. Ocular irritation potential were evaluated and therapeutic efficacy was measured by reduction in intraocular pressure (IOP) in normotensive rabbits. Maximum yield was obtained when the ratio of water/isopropyl alcohol was 1/4 at 55°C. The FT-IR, DSC and ¹³C NMR confirmed the formation of an ether linkage between hydroxyl groups of CS and MCA. The particle size and zeta potential of optimised CSNPs was 250.3 ± 2.62 nm and +33.47 ± 0.723 mV, whereas those for OCM-CSNPs were 187.1 ± 2.72 nm and 30.87 ± 0.86 mV. The entrapment efficiency was significantly improved for OCM-CSNPs, compared to CSNPs. OCM-CSNPs had tailored drug release and improved bioavailability with reduction in pulse entry as compared to CSNPs. Hence, it can be concluded that DRZ loaded OCM-CSNPs would be better alternative option to available eye drops for glaucoma treatment.

The use of mucoadhesive biopolymers is one of the best approaches to prolong the drug residence inside the cul-de-sac, consequently increasing the bioavailability. Thus, the focus of this work was to develop mucoadhesive microspheres to overcome the limitations of ocular drug delivery. The chitosan-sodium alginate microspheres of azelastine hydrochloride were fabricated using modified ionotropic gelation technique. The particle size, zeta potential, entrapment efficiency and drug release kinetics were evaluated and characterized by SEM, FT-IR, DSC, in vitro mucoadhesion and in vivo study. The microspheres had average particle size in the range of 3.55 to 6.70 µm and zeta potential +24.55 to +49.56 mV. The fabricated microspheres possess maximum drug entrapment of 73.05% with 65% mucin binding efficiency and revealed a controlled release over the 8-h period following a non-Fickian diffusion. SEM showed that microspheres were distinct solid with irregular shape. FT-IR and DSC results concluded the drug entrapment into microspheres. In vivo studies on ocular rat model revealed that azelastine microspheres had better efficacy. Chitosan sodium alginate microspheres prepared were in particle size range suitable for ocular purpose. In vitro release and in vivo efficacy studies revealed that the microspheres were effective in prolonging the drug’s presence in cul de sac with improved therapeutic efficacy.

The objective of present study was to develop nonionic surfactant vesicles of proteolytic enzyme serratiopeptidase (SRP) by adapting reverse phase evaporation (REV) technique and to evaluate the viability of SRP niosomal gel in treating the topical inflammation. The feasibility of SRP niosomes by REV method using Span 40 and cholesterol has been successfully demonstrated in this investigation. The entrapment efficiency was found to be influenced by the molar ratio of Span 40 : cholesterol and concentration of SRP in noisome. The developed niosomes were characterized for morphology, particle size, andin vitrorelease. Niosomal gel was prepared by dispersing xanthan gum into optimized batch of SRP niosomes.Ex vivopermeation andin vivoanti-inflammatory efficacy of gel formulation were evaluated topically. SRP niosomes obtained were round in nanosize range. At Span 40 : cholesterol molar ratio 1 : 1 entrapment efficiency was maximum, that is, 54.82% ± 2.08, and showed consistent release pattern. Furthermoreex vivoskin permeation revealed that there was fourfold increase in a steady state flux when SRP was formulated in niosomes and a significant increase in the permeation of SRP, from SRP niosomal gel containing permeation enhancer.In vivoefficacy studies indicated that SRP niosomal gel had a comparable topical anti-inflammatory activity to that of dicolfenac gel.