The construction industry urgently requires sustainable alternatives to conventional cement to mitigate its environmental footprint, which includes 8% of global CO₂ emissions. This review critically examines the potential of rice husk ash (RHA) and silica fume (SF)—industrial and agricultural byproducts—as high-performance supplementary cementitious materials (SCMs) in soil–cement composites. Their pozzolanic reactivity, microstructural enhancement mechanisms, and durability improvements (e.g., compressive strength gains of up to 31.7% for RHA and 250% for SF) are analyzed. This study highlights the synergistic effects of RHA/SF blends in refining pore structure, reducing permeability, and enhancing resistance to chemical attacks. Additionally, this paper quantifies the environmental benefits, including CO₂ emission reduction (up to 25% per ton of cement replaced) and resource recovery from agricultural/industrial waste streams. Challenges such as material variability, optimal dosage (10–15% RHA, 5–8% SF), and regulatory barriers are discussed, alongside future directions for scalable adoption. This work aligns with SDGs 9, 11, and 12, offering actionable insights for sustainable material design.

In this article, the strength characteristics of the cement mortar with waste glass powder of different size and content at different ages were studied. The mechanism of strength development was analysed from the microstructure of mortar specimens based on scanning electron microscopy (SEM) and electronic dispersive spectroscopy (EDS). The results show that the compressive strength and flexural strength of the mortar specimens increase significantly with a higher age. There is an optimal content of glass powder corresponding to the maximum strength. The glass powder of smaller particle size clearly promotes the development of compressive strength and flexural strength in the mortar specimens. It is found from SEM-EDS that glass cement mortar has a larger amount of internal hydration products and higher density compared with ordinary cement mortar. The density of cement mortar incorporating 15 wt% glass powder increases gradually with the decrease of glass particle size. The hydration products and compactness of the cement mortar adding 200–500 mesh glass powder experience an increase and then a decrease with a rise in the glass content. The strength enhancement with the addition of glass powder are mainly attributed to the microaggregate filling effect and pozzolanic effect of the glass powder, as well as to changes in the interfacial transition zone.

High-strength bolted connections are fundamental load-bearing components in critical engineering infrastructures such as wind turbines, bridges, and heavy machinery. Under complex service environments involving dynamic loading, vibration, corrosion, and temperature variations, bolts are prone to interacting failure mechanisms, including fatigue fracture, corrosion-assisted cracking, hydrogen embrittlement, and progressive preload loss, which pose significant challenges for reliable condition monitoring and early fault diagnosis. This review provides a structured synthesis of recent advances in bolt health monitoring and intelligent fault diagnosis. A unified framework is established to link multi-physics failure mechanisms with multi-modal sensing technologies and data-driven diagnostic methods. Key sensing approaches—such as piezoelectric impedance techniques, ultrasonic phased array inspection, and computer vision-based monitoring—are critically reviewed in terms of their physical principles, diagnostic capabilities, and limitations. Furthermore, the transition from traditional model-based and signal-processing-driven methods to machine learning- and deep learning-based approaches is examined, with emphasis on multi-modal data fusion, real-time monitoring, and lifecycle-oriented health management enabled by IoT and digital twin technologies. Finally, key challenges and future research directions toward robust and scalable intelligent bolt health management systems are outlined. This review’s primary contribution lies in establishing a novel, integrated framework that links failure physics to sensing and diagnosis, thereby providing a structured roadmap for transitioning from isolated component monitoring to lifecycle-oriented, intelligent health management systems for critical bolted connections.

By incorporating waste glass into concrete-filled steel tube columns, this study aims to mitigate the environmental impacts associated with the production of cement and concrete while simultaneously reducing costs. This research investigates the effects of replacing the cement in concrete with an equal mass of waste glass powder (WGP) at five different replacement rates—0%, 5%, 15%, 30%, and 60%—and focuses on the mechanical behaviors and value coefficients of concrete-filled steel tubes (CFSTs), which are evaluated through axial compression tests and value engineering methods. The results indicate that the loading process for waste glass powder CFST (WGPCFST) short columns closely resembles that of ordinary CFST short columns. While the bearing capacity of WGPCFST short columns decreased with an increasing WGP content, no significant reduction was observed compared to ordinary CFST short columns. Notably, at replacement rates of 5% to 15%, WGPCFST short columns exhibited an enhanced deformational capacity—at least 14% greater—compared to their ordinary counterparts, suggesting that WGPCFSTs are a promising alternative to CFSTs. Additionally, value engineering results revealed that the highest integrated value was achieved at a WGP replacement rate of 5%. Furthermore, a significant negative correlation was found between the value coefficient and the WGP replacement rate.

To address the issues of excessive cement and energy consumption in ultra-high performance concrete (UHPC), waste glass powder (WGP) was utilized to replace cement at varying rates of 0%, 10%, 20%, and 30% to prepare UHPC. The results indicated that the incorporation of WGP influenced the flowability of UHPC, although it concurrently reduced its mechanical properties. When WGP was utilized at a specific replacement rate of 10%, it was found to enhance the mechanical properties during the later stages of curing (60 and 90 days). Notably, at a WGP replacement rate of 10%, the compressive strength and flexural strength at 90 days of curing reached peak values of 173.1 and 36.4 MPa, respectively. WGP exhibited effective micro-aggregate filling and pozzolanic effects; however, excessive replacement rates led to an increased Ca/Si ratio in the C-S-H gel, resulting in reduced structural compactness and compromised performance of UHPC.

In order to save natural resources and protect the natural environment, the relevant performance of waste glass powder as a building material must be enhanced. In general, volcanic ash activity is enhanced through grinding the glass powder particles to a specific degree of fineness, thereby improving the overall strength of cementitious sand. Our current need is to study the effects of replacing standard sand with glass powder of varying particle size and dosage range on its resistance to sulfate erosion as well as the corresponding mechanisms. To further examine the durability properties of glass powder cementitious sand, this study uses glass powder of 100–200 mesh and 200–500 mesh to create cementitious sand samples, replacing 10% and 15% of standard sand with equal volume. After curing for 28 days in a standard curing room, the samples are submerged in tap water and a 5% concentration of sodium sulfate solution for 30, 60, 90, 120, and 150 days. Subsequently, the mass loss rate, flexural strength, and compressive strength are measured to reflect the sulfate erosion resistance of the cementitious sand samples containing glass powder. The findings indicate that the flexural and compressive strengths of cementitious sand with waste glass powder experience a swift decline in strength during the pre-erosion stage and a slow decline or even an increase in strength during the post-erosion stage as erosion age progresses. As the glass powder dosage increases, there is a noticeable decrease in the flexural and compressive strengths, in which the doping of 200–500 mesh doped with 15% of glass powder has the worst effect on the resistance to sulfate erosion. As the particle size increases, both flexural and compressive strengths significantly improve, suggesting that sulfate erosion properties are gradually enhanced. The primary reason for this phenomenon is that when glass powder substitutes fine aggregate, the activity develops more slowly in the initial stage, primarily filling the pores and cracks. However, the activity increases rapidly later, more fully integrating with the cement mortar in sodium hydroxide’s hydration product to create dense hydrated calcium silicate crystals. This enhances the overall strength of the sample, filling the pore structure within the system, and is more conducive to resisting the erosion effect of sulfate ions on the sample.