In this article, calcium sulfonate complex grease with different polymorphs was acquired. With reference to the improved rolling stability test method, 5% and 10% water were added to the calcium sulfonate composite grease respectively. The influence of water on the flow and deformation characteristics of grease under external force was characterized by rheological analysis. Moreover, the influence of water on the tribological behaviors of grease was evaluated at 30 and 80 °C. The results indicate that water could affect the flow and deformation characteristics of calcium sulfonate complex grease in vaterite polymorph (CSCG-V) more than calcium sulfonate complex grease in calcite polymorph (CSCG-C), and CSCG-V could combine with water to form a more stable grease under external force. Tribological results also clearly show that CSCG-C with water shows better tribological properties than CSCG-V with water under harsh conditions. There was no significant difference in the components of the films that consisted of CaCO₃ and CaO regardless of grease within or without water. The improvement of tribological properties of CSCG-C with 5% and 10% water benefited from the influence of water on the film forming capacity of calcium carbonate on the steel surface.

In this study, Zr active species were implanted into a ZSM-5 zeolite framework to form a solid acid catalyst through steam treatment and the liquid-solid isomorphous substitution process. The as-synthesized Zr-ZSM-5-st catalyst ensured excellent esterification of trimethylolpropane and fatty acids (FAs) to achieve a polyol ester production yield of 94.41%. Combined with N₂ physisorption, X-ray diffraction, Fourier transform infrared spectroscopy, ultraviolet-visible spectroscopy, transmission electron microscopy mapping, X-ray photoelectron spectroscopy, NH₃ temperature-programmed desorption, and inductively coupled mass plasma spectroscopy were conducted. The results revealed that the excellent performance of Zr-ZSM-5-st catalyst could be attributed to the enhanced acidity and the developed surface area and pore structure.