In this work, the intrinsic reason for the premature failure of a 316 stainless steel heat exchanger tube in geothermal water environment is disclosed. The chemical composition of the tube was tested, and the microstructure was examined for material inspection. Fracture morphology and secondary cracks were analyzed, and electron backscattered diffraction was applied to explore the crack propagation mode. The corrosion morphology was observed. The electrochemical behavior was studied with cyclic polarization and double-loop electrochemical potentiokinetic reactivation. It is found that the main failure cause was stress corrosion cracking (SCC). Attacked by chloride ions, the tube is susceptible to SCC under the residual stress as a result of the substandard Mo and Ni content. The SCC mechanism is localized anodic dissolution, and the propagation mode is a mixture of transgranular SCC and intergranular SCC.

This work explored a new idea for enhancing the resistance to stress corrosion cracking (SCC) of mining anchor steel through microalloying. Microalloyed anchor steels with Nb, Cu, Ni, Sb, and C were prepared through vacuum smelting and hot rolling. Electrochemical measurements, slow strain rate tensile (SSRT) tests, and fracture morphology observations were used to study the electrochemical and SCC behavior in the simulated mine environment. The results proved that the microstructure of microalloyed steels varies slightly. Adding Ni, Cu, and Sb can improve the mechanical properties of the anchor steel, while reducing C content decreases tensile strength as a result of loss of the solution-strengthening effect. The addition of Sb, Cu, Ni, and reducing the content of C enhances the resistance to corrosion and SCC by mitigating anodic dissolution (AD), while adding Nb improves SCC resistance by inhibiting hydrogen embrittlement (HE). The combined addition of 1% Ni, 0.5% Cu, 0.05% Nb, 0.1% Sb, and 0.5% C presented the highest SCC resistance, which is a promising prospect for the development of high-performance, low-alloy anchor steels. The combined addition of 1% Ni, 0.5% Cu, 0.05% Nb, and 0.1% Sb resulted in the inhibition of electrochemical reactions and corrosion. As a result of the synergistic effect of the microalloy, both AD and HE mechanisms were simultaneously inhibited, which greatly enhanced SCC resistance.