The surface morphology of Mg-Al-layered double hydroxide (LDH) was successfully controlled by reconstruction during systematic phase transformation from calcined LDH, which is referred to as layered double oxide (LDO). The LDH reconstructed its original phase by the hydration of LDO with expanded basal spacing when reacted with water, including carbonate or methyl orange molecules. During the reaction, the degree of crystal growth along the ab-plane and stacking along the c-axis was significantly influenced by the molecular size and the reaction conditions. The lower concentration of carbonate gave smaller particles on the surface of larger LDO (2000 nm), while the higher concentration induced a sand-rose structure. The reconstruction of smaller-sized LDH (350 nm) did not depend on the concentration of carbonate due to effective adsorption, and it gave a sand-rose structure and exfoliated the LDH layers. The higher the concentration of methyl orange and the longer the reaction time applied, the rougher the surface was obtained with a certain threshold point of the methyl orange concentration. The surface roughness generally increased with the loading mount of methyl orange. However, the degree of the surface roughness even increased after the methyl orange loading reached equilibrium. The result suggested that the surface roughening was mediated by not only the incorporation of guest molecules into the LDH but also a crystal arrangement after a sufficient amount of methyl orange was accommodated.

Metal oxides (MOs) having Mg and Al with Mg/Al ratios of 1, 2, 3, and 4 were synthesized via calcination of the layered double hydroxides (LDH). The X-ray diffraction analysis revealed that all the MO consisted of periclase (MgO) crystallite with comparable crystallinity regardless of the metal ratio. According to the ²⁷Al magic-angle spinning nuclear magnetic resonance, the phase transformation from LDH to MO upon calcination facilitated the evolution of the Al³⁺ ions with unsaturated coordination at the surface of MO. The specific surface area values of MOs were not significantly different from each other, ranging between 100 and 200 m²/g, suggesting that the metal ratio did not strongly influence the porous structure of MO. The temperature-dependent desorption of ammonia demonstrated that the Lewis acidity of the Al-rich MOs was the largest with an Mg/Al ratio of 1, attributed to the efficient exposure of the surface-active site Al³⁺-O²⁻ pairs. The acidity of heterogenous Al-rich MOs significantly increased with the exposed tetrahedral Al site on the surface and dramatically diminished when the molar ratio (Mg/Al) was over two.

Release of ferulic acid from surface-functionalized hollow nanoporous silica particles (HNSPs) was investigated in deionized water (DI water) and in ethanol. The host material, an HNSP, was synthesized in the presence of polymer and surfactant templates, and the pore as well as the surface were modified with either pentyltriethoxysilane (PTS) or octyltriethoxysilane (OTS) through silane coupling reactions. The inner hollow space occupied a volume of ~45% of the whole HNSP with a 2.54 nm pore channel in the wall. The pore size was estimated to decrease to 1.5 nm and 0.5 nm via the PTS and OTS functionalization, respectively. The encapsulation efficiencies of the HNSP (25 wt%), PTS-functionalized HNSP (PTS-HNSP, 22 wt%) and OTS-functionalized HNSP (OST-HNSP, 25 wt%) toward ferulic acid were similar, while the %release in DI water and ethanol varied following HNSP > PTS-HNSP > OTS-HNSP. Release kinetic analyses with Korsmeyer–Peppas fitting suggested a trade-off relationship between the solvent’s ability to access the HNSP and the affinity of ferulic acid to the surface, allowing us to understand the solvent’s controlled release rate and mechanism.

Cinnamic acid (CA) was successfully incorporated into Zn-Al layered double hydroxide (LDH) through coprecipitation. The CA moiety was stabilized in the interlayer space through not only electrostatic interaction but also intermolecular π-π interaction. It was noteworthy that the CA arrangement was fairly independent of the charge density of LDH, showing the important role of the layer–CA and CA-CA interactions in molecular stabilization. Computer simulations using the Monte Carlo method as well as analytical approaches including infrared, UV-vis spectroscopy, and differential scanning calorimetry showed the existence of intermolecular interaction. In order to reinforce molecular stabilization, a neutral derivative of CA, cinnamaldehyde (CAD), was additionally incorporated into LDH. It was clearly shown that CAD played a role as a π-π interaction mediator to enhance the stabilization of CA. The time-dependent release of CA from LDH was first governed by the layer charge density of LDH; however, the existence of CAD provided additional stabilization to the CA arrangement to slow down the release kinetics.

The inner lumen of the polyurethane tube is modified with titanium dioxide particles and polyethylene glycol chains to create an anti-biofouling tracheostomy tube with integrated physical, chemical, and mechanical functionalities. The surface of tube is initially midified with titanium dioxide particles utilizing polyurethane binder via dip-coating, followed by further functionalization with polyethylene glycol chains. The infrared spectrum confirms that all coating components are securely attached to the inner lumen of medical tube. Scanning electron microscopy and surface hardness tests validate that the coated layer is highly homogeneous, containing various coating agents, and remains stable under mechanical stimulation. The extraction test, conducted according to International Standards Organization guideline, indicates no significant release of the coated agents under physiological conditions; additionally, the extract shows neither cytotoxicity against bronchial cells nor sensitization on animal skin. By achieving a physically roughened surface, chemically modifying with titanium dioxide, and adding a mechanical repellent in the form of polyethylene glycol chains, the surface of tube acquires comprehensive antifouling properties. Consequently, the coated tube exhibits up to an 85.54 % reduction in biofouling compared with a bare polyurethane tube.