Graphene, or single-layered graphite, with its high crystallinity and interesting semimetal electronic properties, has emerged as an exciting two-dimensional material showing great promise for the fabrication of nanoscale devices. Thin, elongated strips of graphene that possess straight edges, termed graphene ribbons, gradually transform from semiconductors to semimetals as their width increases, and represent a particularly versatile variety of graphene. Several lithographic, chemical and synthetic procedures are known to produce microscopic samples of graphene nanoribbons, and one chemical vapour deposition process has successfully produced macroscopic quantities of nanoribbons at 950 degrees C. Here we describe a simple solution-based oxidative process for producing a nearly 100% yield of nanoribbon structures by lengthwise cutting and unravelling of multiwalled carbon nanotube (MWCNT) side walls. Although oxidative shortening of MWCNTs has previously been achieved, lengthwise cutting is hitherto unreported. Ribbon structures with high water solubility are obtained. Subsequent chemical reduction of the nanoribbons from MWCNTs results in restoration of electrical conductivity. These early results affording nanoribbons could eventually lead to applications in fields of electronics and composite materials where bulk quantities of nanoribbons are required.

Despite intensive research, the mechanism of graphene oxide (GO) formation remains unclear. The role of interfacial interactions between solid graphite and the liquid reaction medium, and transport of the oxidizing agent into the graphite, has not been well-addressed. In this work, we show that formation of GO from graphite constitutes three distinct independent steps. The reaction can be stopped at each step, and the corresponding intermediate products can be isolated, characterized, and stored under appropriate conditions. The first step is conversion of graphite into a stage-1 graphite intercalation compound (GIC). The second step is conversion of the stage-1 GIC into oxidized graphite, which we define as pristine graphite oxide (PGO). This step involves diffusion of the oxidizing agent into the preoccupied graphite galleries. This rate-determining step makes the entire process diffusive-controlled. The third step is conversion of PGO into conventional GO after exposure to water, which involves hydrolysis of covalent sulfates and loss of all interlayer registry.