In the present study, MoO₃:MoS₂ hybrid thin layers have been synthesized through partial oxidation of MoS₂. We have demonstrated that the reaction requires darkness conditions to decrease the oxidation rate, thus obtaining the hybrid, MoO₃:MoS₂. A simple liquid-phase exfoliation (LPE) is carried out to achieve homogenous MoS₂ nanoflakes and high reproducibility of the results after MoS₂ oxidation. XPS analyses reveal the presence of MoO₃, MoS₂, and MoOxSy in the hybrid layer. These results are also confirmed by X-ray diffraction and high-resolution TEM. Optical absorbance reveals that the absorption peaks of the MoO₃:MoS₂ hybrid are slightly redshifted with the appearance of absorption peaks in the near-infrared region due to the defects created after the oxidation reaction. The composition and atomic percentages of each component in the hybrid layer as a function of reaction time have also been reported to give perspective guides for improving electronic and optoelectronic devices based on 2D-MoS₂.

Ternary planar heterojunction organic solar cells (PHJ-OPVs) were fabricated using three organic small molecules, alpha-sexithiophene (α-6T), aluminum phthalocyanine chloride (AlPcCl) and fullerene (C₆₀). These molecules can be easily sublimated under a vacuum; they have complementary optical absorption spectra and their energy band structure alignment is favorable for electronic charge transfers. Moreover, α-6T and AlPcCl have almost the same HOMO, which is desirable to avoid any decrease in open circuit voltage. The AlPcCl intercalated layer bridges the energy levels of the electron donor, α-6T, and the electron acceptor, C₆₀, which facilitates charge transport through the energy cascade effect. Moreover, the charge carrier mobility measurements of AlPcCl, using the space charge limited current method, demonstrated that it iss ambipolar. All these properties combine to improve the power conversion efficiency (PCE) of PHJ-OPVs by moving from binary structures (α-6T/C₆₀, α-6T/AlPcCl and AlPcCl/C₆₀) to ternary ones (α-6T/AlPcCl/C₆₀). We show, in this study, that both interfaces of the ternary PHJ-OPVs are efficient for carrier separation. After optimization of the different layer thickness, we show that, by comparing the optimum efficiencies of the binary PHJ-OPVs, the realization of ternary PHJ-OPVs, based on the active layers α-6T/AlPcCl/C₆₀, using the following optimized method, allows us to achieve a PCE of 4.33%.