Bimetallic phosphide (Ni_xFe_1−x)₂P hollow nanocubes were prepared from PBAs as highly active and stable OER electrocatalysts.

Highly monodisperse Ni NPs in UiO-66 give both excellent activity and selectivity for CO ₂ methanation at low temperatures.

Graphitic carbon nitride (g-C₃N₄) is a promising candidate for visible-light-driven photocatalytic water splitting. However, some inherent drawbacks of g-C₃N₄, such as poor charge separation and transfer efficiencies, limited optical absorption and a low surface area, restrain its performance in photocatalytic hydrogen evolution. To solve these problems, in this study, a series of phosphorus (P) doped g-C₃N₄ (PCN) samples are prepared by direct thermolysis of a mixture of urea and 4-(diphenylphosphino)benzoic acid (4-DPPBA). P atoms have been successfully introduced into the framework of g-C₃N₄ by forming P–N bonds. The as-obtained samples are investigated for photocatalytic water splitting under visible light. Results reveal that the optimal PCN sample exhibits a high hydrogen evolution rate of 2610.80 μmol h⁻¹ g⁻¹ (λ ≥ 420 nm) in the presence of a sacrificial agent, which is almost 10 times higher than that of bare g-C₃N₄ (265.00 μmol h⁻¹ g⁻¹). This is mainly ascribed to the fact that electron-rich P atoms, acting as an electron donor, efficiently trap photogenerated holes and substantially suppress the recombination of charge carriers. Besides, the introduction of P atoms modifies the surface properties, narrows the band gap and increases the electrical conductivity. A possible mechanism is proposed for the photocatalytic reaction over PCN samples. Moreover, the PCN samples maintain high photocatalytic activity and chemical stability after recycling experiments, making them promising materials with broad application prospects in solar-to-fuel conversion.

A single-atom dispersed Ni doping strategy to boost the performance of N–C materials for CO₂RR by the pyrolysis of a metal–organic molecule complex was reported and revealed.