Natural-chlorophyll-related porphyrins, including (2H, Zn, Cu)-protoporphyrin IX (Por-1) and Zn-mesoporphyrin IX (Por-2), and chlorins, including chlorin e₆ (Chl-1), chlorin e₄ (Chl-2), and rhodin G₇ (Chl-3), have been used in dye-sensitized solar cells (DSSCs). For porphyrin sensitizers that have vinyl groups at the β-positions, zinc coordinated Por-1 gives the highest solar-energy-to-electricity conversion efficiency (h) of up to 2.9%. Replacing the vinyl groups of ZnPor-1 with ethyl groups increases the open-circuit voltage (V_oc) from 0.61 V to 0.66 V, but decreases the short-circuit current (J_sc) from 7.0 mA·cm⁻² to 6.1 mA·cm⁻² and the value of h to 2.8%. Density functional theory (DFT) and time-dependent DFT (TD-DFT) calculations suggest that the higher J_sc values of Zn-based porphyrin sensitizers result from the favorable electron injection from the LUMO at higher energy levels. In the case of the chlorin sensitizers, the number of carboxyl protons has a large effect on the photovoltaic performance. Chl-2 with two carboxyl protons gives much higher values of J_sc, V_oc, and h than does Chl-1 with three carboxyl protons. Replacing the protons of Chl-1 with sodium ions can substantially improve the photovoltaic performance of Chl-1-based solar cells. Furthermore, the sodium salt of Chl-3 with an aldehyde group at the C7 position shows poorer photovoltaic performance than does the sodium salt of Chl-1 with methyl groups at the C7 position. This is due to the low light-harvesting capability of Chl-3.

A donor-acceptor (D-A) type indoline dye, D149, was used as an electron donor in solution-processed organic solar cells (OSCs). For bulk-heterojunction (BHJ) type OSCs with PC₇₀BM as electron acceptor, the power conversion efficiency (PCE) is sensitive to the amount of D149 in the D149/PC₇₀BM blend film. When the concentration of D149 in the blend film was as low as 5%, the highest PCE of up to 1.29%, together with a short-circuit current density (Jsc) of 4.58 mA·cm⁻², an open-circuit voltage (Voc) of 0.90 V and a fill factor (FF) of 0.31, was achieved. In order to improve the PCE of D149-based OSCs, a bilayer-heterojunction configuration with C₇₀ as electron acceptor has been employed. By optimizing the thickness of the D149 layer and varying the electron- and hole-transport layers, a highest PCE of up to 2.28% with a Jsc of 4.38 mA·cm⁻², a Voc of 0.77 V, and an FF of 0.62 was achieved under AM 1.5G solar illumination (100 mW·cm⁻²).